Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Strength | 414 MPa @Temperature 23.9 °C |
60000 psi @Temperature 75.0 °F |
Dry; ASTM D695 |
Park Electrochemical Nelcote® E-722 Epoxy Prepreg, 7781 E-Glass Reinforced Nelcote® E-722 is a modified 350°F cure epoxy system with excellent processing characteristics for vacuum bag, press, and autoclave molding.Key Features and Benefits:Epoxy resin system optimized f.. |
|||
Compressive Strength | 414 MPa @Temperature 149 °C |
60000 psi @Temperature 300 °F |
Dry; ASTM D695 |
Park Electrochemical Nelcote® V-376 Cyanate Ester Epoxy Prepregs, 581 Quartz Reinforced Nelcote® V-376 is a Cyanate Ester matrix providing excellent electrical and mechanical properties for harsh aircraft, shipboard, and undersea applications for Radomes, Antenna, and Reflectors. Simp.. |
|||
Compressive Strength | 414 MPa | 60000 psi | |
Pyrotek TS-110 Thermoset Electrical Insulation Product (Nema Grade: G-10) Glass reinforcement, Epoxy Resin, Natural Color. High flexural, impact and bond strength at room temperature.Information provided by Pyrotek. |
|||
Compressive Strength | 414 MPa @Thickness 12.7 mm |
60000 psi @Thickness 0.500 in |
Flatwise |
Industrial Laminates/Norplex NP841 Glass Fabric
(discontinued **) Description: Woven glass fabric with phenolic resin. Contains Kocite® for controlled conductivity. Acts as static electricity drain to protect electrical and electronic equipment.Thickness Tested: .. |
|||
Compressive Strength | 414 MPa | 60000 psi | Axial; ASTM D695 |
Glastic Laminates/Shapes HIR Grade HIR Fiberglass-Reinforced Polyester Rod Data provided by Glastic Corporation.A continuous-filament fiberglass-roving provides superior strength. Highest physical properties of GLASROD series. |
|||
Compressive Strength | >= 414 MPa | >= 60000 psi | |
3M W-210 Ceramic Microspheres 3M™ White Ceramic Microspheres are unique, semi-transparent, white-colored, fine particle size, high-strength microspheres. These products are typically used to reduce VOC levels; increase filler l.. |
|||
Compressive Strength | >= 414 MPa | >= 60000 psi | |
3M W-410 Ceramic Microspheres 3M™ White Ceramic Microspheres are unique, semi-transparent, white-colored, fine particle size, high-strength microspheres. These products are typically used to reduce VOC levels; increase filler l.. |
|||
Compressive Strength | >= 414 MPa | >= 60000 psi | |
3M W-610 Ceramic Microspheres 3M™ White Ceramic Microspheres are unique, semi-transparent, white-colored, fine particle size, high-strength microspheres. These products are typically used to reduce VOC levels; increase filler l.. |
|||
Compressive Strength | >= 414 MPa | >= 60000 psi | |
Potters Industries A-Series Z-CEL® 8054 White Synthetic Sodium Aluminosilicate Microsphere Fine particle white spheres developed as filler for paints, coatings and films.Information provided by Potters Industries. |