Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 250 MPa @Thickness >=1.50 mm |
36300 psi @Thickness >=0.0591 in |
24hr/23°C/50% RH; ISO 527; IEC/EN 60893-2 5.6 |
Elektro-Isola G-Etronax B Phenolic, Glass Fabric Reinforcement, Dark Brown, Sheet High performance/price ratio insulation material. Self-extinguishing, halogen-free, very low smoke emission and toxicity. Mechanically much stronger than the Etronit and Etronax types.Information pr.. |
|||
Tensile Strength | 250 MPa @Thickness >=1.50 mm |
36300 psi @Thickness >=0.0591 in |
24hr/23°C/50% RH; ISO 527; IEC/EN 60893-2 5.6 |
Elektro-Isola G-Etronax M Melamine, Glass Fabric Reinforcement, White, Sheets Description: Melamine-based composite material reinforced with glass fabric. High arc resistance and tracking resistance. Flame-resistant. Self-extinguishing.Information provided by Elektro-Isola |
|||
Tensile Strength | >= 250 MPa | >= 36300 psi | IEC 1212-2 5.7 |
Hippe EP GM 202 Glass Mat Reinforced Epoxy Resin - Sheet |
|||
Tensile Strength | >= 250 MPa | >= 36300 psi | IEC 1212-2 5.7 |
Hippe PI GC 301 Woven Glass Cloth Reinforced Phenolic Sheet Used in electrical and mechanical applications. Very good mechanical and electrical properties at high temperature.Information provided by Hippe. |
|||
Tensile Strength | >= 250 MPa | >= 36300 psi | IEC 1212-2 5.7 |
Hippe EP GM 201 Glass Mat Reinforced Epoxy Resin - Sheet Used in mechanical and electrical applications. Extremely high mechanical strength at moderate temperature. Very good electrical properties under high humidity.Information provided by Hippe. |
|||
Tensile Strength | >= 250 MPa | >= 36300 psi | IEC 1212-2 5.7 |
Hippe EP GM 203 Glass Mat Reinforced Epoxy Resin - Sheet |
|||
Tensile Strength | >= 250 MPa | >= 36300 psi | IEC 1212-2 5.7 |
Hippe EP GM 204 Glass Mat Reinforced Epoxy Resin - Sheet |
|||
Tensile Strength | 250 MPa | 36300 psi | y; IPC TM-650 2.4.18.3 |
Arlon 35N Fast Cure Polyimide Laminate and Prepreg High reliability and high temperature material35N is a pure polyimide laminate and prepreg system for applications requiring high temperature performance. High Tg results in low Z-direction expansi.. |