Elektro-Isola G-Etronax M Melamine, Glass Fabric Reinforcement, White, Sheets

Category Polymer , Thermoset , Melamine , Melamine Formaldehyde, Molded, Glass Fiber Filler
Manufacturer Elektro-Isola
Trade Name G-Etronax
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Elektro-Isola G-Etronax M Melamine, Glass Fabric Reinforcement, White, Sheets.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Melamine-based composite material reinforced with glass fabric. High arc resistance and tracking resistance. Flame-resistant. Self-extinguishing.Information provided by Elektro-Isola
Physical Properties Metric English Comments
Density 2.00 g/cc
0.0723 lb/in³
24hr/23°C/50% RH; ISO 1183-A; IEC/EN 60893-2 8.1
Water Absorption 2.53 %
2.53 %
24hr/50°C+24hr in water at 23°C,Test Specimen 50x50x3[mm]; ISO 62-1; IEC/EN 60893-2 8.2
Mechanical Properties Metric English Comments
Tensile Strength 250 MPa

@Thickness >=1.50 mm
36300 psi

@Thickness >=0.0591 in
24hr/23°C/50% RH; ISO 527; IEC/EN 60893-2 5.6
Modulus of Elasticity 18.0 GPa

@Thickness >=1.50 mm
2610 ksi

@Thickness >=0.0591 in
24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.2
Flexural Strength 350 MPa

@Thickness >=1.50 mm
50800 psi

@Thickness >=0.0591 in
24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1
Compressive Strength 450 MPa

@Thickness >=5.00 mm
65300 psi

@Thickness >=0.197 in
24hr/23°C/50% RH; ISO 604; IEC/EN 60893-2 5.3
Shear Strength 30.0 MPa

@Thickness >=5.00 mm
4350 psi

@Thickness >=0.197 in
24hr/23°C/50% RH; IEC/EN 60893-2 5.5
Izod Impact, Notched (ISO) 60.0 kJ/m²

@Thickness >=5.00 mm
28.6 ft-lb/in²

@Thickness >=0.197 in
24hr/23°C/50% RH; ISO 180/2A; IEC/EN 60893-2 5.4.3
Thermal Properties Metric English Comments
Maximum Service Temperature, Inert 130 °C

@Thickness 0.000 mm,
Time 7.20e+7 sec
266 °F

@Thickness 0.000 in,
Time 20000 hour
IEC 60216; IEC/EN 60893-2 7.1
Flammability, UL94 V-0
V-0
IEC/EN 60893-2 7.2; IEC 60695-11-10
Electrical Properties Metric English Comments
Insulation Resistance 1.00e+8 ohm

@Thickness >=3.00 mm
1.00e+8 ohm

@Thickness >=0.118 in
24hr/50°C+24h in water at 23°C; IEC 60167; IEC/EN 60893-2 6.3
Dielectric Constant 5.5

@Thickness <=3.00 mm,
Frequency 50.0 Hz
5.5

@Thickness <=0.118 in,
Frequency 50.0 Hz
96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
Dielectric Strength 0.800 kV/mm

@Thickness >=3.00 mm
20.3 kV/in

@Thickness >=0.118 in
24hr/23°C/50% RH+1hr/oil 90°C; Parallel; IEC 60245-1; IEC/EN 60893-2 6.1.3.2
5.00 kV/mm

@Thickness 3.00 mm
127 kV/in

@Thickness 0.118 in
24hr/23°C/50% RH+1hr/oil 90°C; Perpendicular; IEC 60245-1; IEC/EN 60893-2 6.1.3.1
Dissipation Factor 0.010

@Frequency 50.0 Hz
0.010

@Frequency 50.0 Hz
96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
Comparative Tracking Index 600 V

@Thickness 3.00 mm
600 V

@Thickness 0.118 in
IEC 60112; IEC/EN 60893-2 6.4