Solvay Specialty Polymers Amodel® A-1133 HS Polyphthalamide (PPA) (Unverified Data**)

Category	Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers Amodel® A-1133 HS Polyphthalamide (PPA) (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Amodel A-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, high flexural modulus and high tensile strength. Excellent creep resistance and low moisture absorption are also characteristic of this resin. - Black: A-1133 HS BK 324 - Black: A-1133 HS BK 543 - Natural: A-1133 HS NTData is presented for dry polymer unless noted as 'conditioned'.Information provided by Solvay Specialty Polymers.

Physical Properties	Metric	English	Comments
Density	1.48 g/cc	0.0535 lb/in³	ISO 1183/A
Filler Content	33 %	33 %	Glass Fiber Reinforcement
Water Absorption	0.21 % @Time 86400 sec	0.21 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.0040 cm/cm	0.0040 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.0080 cm/cm	0.0080 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	125	125	R-Scale; ASTM D785
Tensile Strength at Break	72.0 MPa @Temperature 175 °C	10400 psi @Temperature 347 °F	ISO 527-2
	80.0 MPa @Temperature 150 °C	11600 psi @Temperature 302 °F	ISO 527-2
	148 MPa @Temperature 100 °C	21500 psi @Temperature 212 °F	ISO 527-2
	233 MPa @Temperature 23.0 °C	33800 psi @Temperature 73.4 °F	ISO 527-2
Tensile Strength	193 MPa	28000 psi	Conditioned; ASTM D638
	221 MPa	32100 psi	ASTM D638
Elongation at Break	2.1 %	2.1 %	Conditioned; ASTM D638
	2.5 %	2.5 %	ASTM D638
	2.5 % @Temperature 23.0 °C	2.5 % @Temperature 73.4 °F	ISO 527-2
	2.9 % @Temperature 100 °C	2.9 % @Temperature 212 °F	ISO 527-2
	8.5 % @Temperature 175 °C	8.5 % @Temperature 347 °F	ISO 527-2
	8.7 % @Temperature 150 °C	8.7 % @Temperature 302 °F	ISO 527-2
Tensile Modulus	13.1 GPa	1900 ksi	ASTM D638
	13.1 GPa	1900 ksi	Conditioned; ASTM D638
	4.30 GPa @Temperature 175 °C	624 ksi @Temperature 347 °F	ISO 527-2
	6.70 GPa @Temperature 150 °C	972 ksi @Temperature 302 °F	ISO 527-2
	10.8 GPa @Temperature 100 °C	1570 ksi @Temperature 212 °F	ISO 527-2
	13.4 GPa @Temperature 23.0 °C	1940 ksi @Temperature 73.4 °F	ISO 527-2
Flexural Strength	254 MPa	36800 psi	Conditioned; ASTM D790
	317 MPa	46000 psi	ASTM D790
	80.0 MPa @Temperature 175 °C	11600 psi @Temperature 347 °F	ISO 178
	93.0 MPa @Temperature 150 °C	13500 psi @Temperature 302 °F	ISO 178
	227 MPa @Temperature 100 °C	32900 psi @Temperature 212 °F	ISO 178
	319 MPa @Temperature 23.0 °C	46300 psi @Temperature 73.4 °F	ISO 178
Flexural Modulus	11.4 GPa	1650 ksi	ASTM D790
	11.4 GPa	1650 ksi	Conditioned; ASTM D790
	3.60 GPa @Temperature 175 °C	522 ksi @Temperature 347 °F	ISO 178
	4.00 GPa @Temperature 150 °C	580 ksi @Temperature 302 °F	ISO 178
	9.80 GPa @Temperature 100 °C	1420 ksi @Temperature 212 °F	ISO 178
	11.6 GPa @Temperature 23.0 °C	1680 ksi @Temperature 73.4 °F	ISO 178
Compressive Strength	185 MPa	26800 psi	ASTM D695
Poissons Ratio	0.41	0.41	ASTM E132
Shear Modulus	4.65 - 4.75 GPa	674 - 689 ksi	Calculated
Shear Strength	88.9 MPa	12900 psi	Conditioned; ASTM D732
	101 MPa	14600 psi	ASTM D732
Izod Impact, Notched	0.590 J/cm	1.11 ft-lb/in	Conditioned; ASTM D256
	0.800 J/cm	1.50 ft-lb/in	ASTM D256
	7.70 J/cm	14.4 ft-lb/in	ASTM D256
Izod Impact, Notched (ISO)	8.80 kJ/m²	4.19 ft-lb/in²	ISO 180/1A
Izod Impact, Unnotched (ISO)	49.0 kJ/m² @Temperature 23.0 °C	23.3 ft-lb/in² @Temperature 73.4 °F	ISO 180/1U
Charpy Impact Unnotched	7.30 J/cm²	34.7 ft-lb/in²	ISO 179/1eU
Charpy Impact, Notched	0.950 J/cm²	4.52 ft-lb/in²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	24.0 µm/m-°C @Temperature 0.000 - 100 °C	13.3 µin/in-°F @Temperature 32.0 - 212 °F	TMA; ASTM E831
	27.0 µm/m-°C @Temperature 100 - 200 °C	15.0 µin/in-°F @Temperature 212 - 392 °F	TMA; ASTM E831
CTE, linear, Transverse to Flow	55.0 µm/m-°C @Temperature 0.000 - 100 °C	30.6 µin/in-°F @Temperature 32.0 - 212 °F	ASTM E831
	110 µm/m-°C @Temperature 100 - 200 °C	61.1 µin/in-°F @Temperature 212 - 392 °F	ASTM E831
Melting Point	313 °C	595 °F	ISO 11357-3
	313 °C	595 °F	ASTM D570
Maximum Service Temperature, Air	164 °C @Time 7.20e+7 sec	327 °F @Time 20000 hour	Continuous; ASTM D3045
	185 °C @Time 1.80e+7 sec	365 °F @Time 5000 hour	Continuous; ASTM D3045

Electrical Properties	Metric	English	Comments
Volume Resistivity	2.00e+15 ohm-cm	2.00e+15 ohm-cm	Conditioned; ASTM D257
	1.00e+16 ohm-cm	1.00e+16 ohm-cm	ASTM D257
Dielectric Constant	4.2 @Frequency 1.00e+6 Hz	4.2 @Frequency 1.00e+6 Hz	ASTM D150
	4.3 @Frequency 1.00e+6 Hz	4.3 @Frequency 1.00e+6 Hz	Conditioned; ASTM D150
	4.4 @Frequency 60.0 Hz	4.4 @Frequency 60.0 Hz	ASTM D150
	4.7 @Frequency 60.0 Hz	4.7 @Frequency 60.0 Hz	Conditioned; ASTM D150
Dielectric Strength	21.0 kV/mm @Thickness 3.20 mm	533 kV/in @Thickness 0.126 in	ASTM D149
	21.0 kV/mm @Thickness 3.20 mm	533 kV/in @Thickness 0.126 in	Conditioned; ASTM D149
Dissipation Factor	0.0050 @Frequency 60.0 Hz	0.0050 @Frequency 60.0 Hz	ASTM D150
	0.0090 @Frequency 60.0 Hz	0.0090 @Frequency 60.0 Hz	Conditioned; ASTM D150
	0.017 @Frequency 1.00e+6 Hz	0.017 @Frequency 1.00e+6 Hz	ASTM D150
	0.022 @Frequency 1.00e+6 Hz	0.022 @Frequency 1.00e+6 Hz	Conditioned; ASTM D150
Arc Resistance	120 sec	120 sec	ASTM D495
	140 sec	140 sec	ASTM D495
Comparative Tracking Index	550 V	550 V	UL 746
	550 V	550 V	Conditioned; UL 746