Polymer Property : Linear Mold Shrinkage, Flow = 0.023 in/in Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Flow	0.023 cm/cm @Time 86400 sec	0.023 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP KG002 Acetal Copolymer LNP* LUBRICOMP* KG002 is a compound based on Acetal Copolymer resin containing 10% Graphite. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Flow	0.023 cm/cm @Time 86400 sec	0.023 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP KG002 Acetal Copolymer LNP* LUBRICOMP* KG002 is a compound based on Acetal Copolymer resin containing 10% Graphite. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Flow	0.023 cm/cm @Time 86400 sec	0.023 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP KG002 Acetal Copolymer (Asia Pacific) LNP* Lubricomp* KG002 is a compound based on Acetal Copolymer resin containing Graphite Powder. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.023 cm/cm @Time 86400 sec	0.023 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP KG002 Acetal Copolymer (Asia Pacific) LNP* Lubricomp* KG002 is a compound based on Acetal Copolymer resin containing Graphite Powder. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.023 cm/cm @Time 86400 sec	0.023 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP KL001 Acetal Copolymer LNP* LUBRICOMP* KL001 is a compound based on Acetal Copolymer resin containing 5% PTFE. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Flow	0.023 cm/cm @Time 86400 sec	0.023 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP KL001 Acetal Copolymer LNP* LUBRICOMP* KL001 is a compound based on Acetal Copolymer resin containing 5% PTFE. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Flow	0.023 cm/cm @Time 86400 sec	0.023 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP KL001 Acetal Copolymer (Asia Pacific) LNP* Lubricomp* KL001 is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.023 cm/cm @Time 86400 sec	0.023 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP KL001 Acetal Copolymer (Asia Pacific) LNP* Lubricomp* KL001 is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.023 - 0.025 cm/cm @Time 86400 sec	0.023 - 0.025 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRILOY RX05497 PA 66 LNP LUBRILOY* RX05497 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Flow	0.023 - 0.025 cm/cm @Time 86400 sec	0.023 - 0.025 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRILOY RX05497 PA 66 (Asia Pacific) LNP LUBRILOY* RX05497 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.023 cm/cm @Time 86400 sec	0.023 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Thermocomp KB005 Acetal Copolymer LNP THERMOCOMP* KB005 is a compound based on Acetal Copolymer resin containing Glass Bead.This data was supplied by SABIC-IP for the Americas region.