Polymer Property : Linear Mold Shrinkage, Flow = 0.025 in/in Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Linear Mold Shrinkage, Flow 0.0197 - 0.025 cm/cm

@Time 86400 sec
0.0197 - 0.025 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP LUBRICOMP KL004 Acetal Copolymer
LNP LUBRICOMP* KL004 is a compound based on Acetal Copolymer resin containing 20% PTFE. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Flow 0.0197 - 0.025 cm/cm

@Time 86400 sec
0.0197 - 0.025 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP KL004 Acetal Copolymer
LNP LUBRICOMP* KL004 is a compound based on Acetal Copolymer resin containing 20% PTFE. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Flow 0.0197 - 0.025 cm/cm

@Time 86400 sec
0.0197 - 0.025 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP KL004 Acetal Copolymer (Asia Pacific)
LNP Lubricomp* KL004 is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated. This grade was previously found under the LNP* Fu..
Linear Mold Shrinkage, Flow 0.0197 - 0.025 cm/cm

@Time 86400 sec
0.0197 - 0.025 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP LUBRICOMP KL004 Acetal Copolymer (Asia Pacific)
LNP Lubricomp* KL004 is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated. This grade was previously found under the LNP* Fu..
Linear Mold Shrinkage, Flow 0.0197 - 0.025 cm/cm

@Time 86400 sec
0.0197 - 0.025 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP KL004 Acetal Copolymer (Europe-Africa-Middle East)
LNP* LUBRICOMP* KL004 is a compound based on Acetal Copolymer containing PTFE. Added features include Internally Lubricated.
Linear Mold Shrinkage, Flow 0.0197 - 0.025 cm/cm

@Time 86400 sec
0.0197 - 0.025 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP LUBRICOMP KL004 Acetal Copolymer (Europe-Africa-Middle East)
LNP* LUBRICOMP* KL004 is a compound based on Acetal Copolymer containing PTFE. Added features include Internally Lubricated.
Linear Mold Shrinkage, Flow 0.0197 - 0.025 cm/cm

@Time 86400 sec
0.0197 - 0.025 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP KL004L Acetal Copolymer
LNP* LUBRICOMP* KL004L is a compound based on Acetal Copolymer resin containing 20% PTFE. Added features of this material include: Wear Resistant, Low Extractible.
Linear Mold Shrinkage, Flow 0.0197 - 0.025 cm/cm

@Time 86400 sec
0.0197 - 0.025 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP LUBRICOMP KL004L Acetal Copolymer
LNP* LUBRICOMP* KL004L is a compound based on Acetal Copolymer resin containing 20% PTFE. Added features of this material include: Wear Resistant, Low Extractible.
Linear Mold Shrinkage, Flow 0.0197 - 0.025 cm/cm

@Time 86400 sec
0.0197 - 0.025 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP LUBRICOMP KL004U Acetal Copolymer
LNP LUBRICOMP* KL004U is a compound based on Acetal Copolymer resin containing 20% PTFE. Added features of this material include: Wear Resistant, UV Stabilized.
Linear Mold Shrinkage, Flow 0.020 - 0.025 cm/cm

@Time 86400 sec
0.020 - 0.025 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP KL004U Acetal Copolymer
LNP LUBRICOMP* KL004U is a compound based on Acetal Copolymer resin containing 20% PTFE. Added features of this material include: Wear Resistant, UV Stabilized.
Linear Mold Shrinkage, Flow 0.0197 - 0.025 cm/cm

@Time 86400 sec
0.0197 - 0.025 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP LUBRICOMP KL004U Acetal Copolymer (Asia Pacific)
LNP Lubricomp* KL004U is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated. This grade was previously found under the LNP* F..
Linear Mold Shrinkage, Flow 0.020 - 0.025 cm/cm

@Time 86400 sec
0.020 - 0.025 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP KL004U Acetal Copolymer (Asia Pacific)
LNP Lubricomp* KL004U is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated. This grade was previously found under the LNP* F..
Linear Mold Shrinkage, Flow 0.0197 - 0.025 cm/cm

@Time 86400 sec
0.0197 - 0.025 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP KL004XXC Acetal Copolymer
LNP LUBRICOMP* KL004XXC is a compound based on Acetal Copolymer resin containing 20% PTFE. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Flow 0.0197 - 0.025 cm/cm

@Time 86400 sec
0.0197 - 0.025 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP LUBRICOMP KL004XXC Acetal Copolymer
LNP LUBRICOMP* KL004XXC is a compound based on Acetal Copolymer resin containing 20% PTFE. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Flow 0.0197 - 0.025 cm/cm

@Time 86400 sec
0.0197 - 0.025 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP KL004XXC Acetal Copolymer (Asia Pacific)
LNP LUBRICOMP* KL004XXC is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow 0.0197 - 0.025 cm/cm

@Time 86400 sec
0.0197 - 0.025 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP LUBRICOMP KL004XXC Acetal Copolymer (Asia Pacific)
LNP LUBRICOMP* KL004XXC is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow 0.023 - 0.025 cm/cm

@Time 86400 sec
0.023 - 0.025 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP LUBRILOY RX05497 PA 66
LNP LUBRILOY* RX05497 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Flow 0.023 - 0.025 cm/cm

@Time 86400 sec
0.023 - 0.025 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP LUBRILOY RX05497 PA 66 (Asia Pacific)
LNP LUBRILOY* RX05497 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.