SABIC Innovative Plastics LNP LUBRICOMP KL001 Acetal Copolymer (Asia Pacific)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP KL001 Acetal Copolymer (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* KL001 is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
ISO 1183
1.44 g/cc
0.0520 lb/in³
ASTM D792
Moisture Absorption 0.200 %
0.200 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.023 cm/cm

@Time 86400 sec
0.023 in/in

@Time 24.0 hour
ASTM D955
0.023 cm/cm

@Time 86400 sec
0.023 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.023 cm/cm

@Time 86400 sec
0.023 in/in

@Time 24.0 hour
ASTM D955
0.023 cm/cm

@Time 86400 sec
0.023 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 52.0 MPa
7540 psi
ASTM D638
53.0 MPa
7690 psi
ISO 527
Tensile Strength, Yield 54.0 MPa
7830 psi
ISO 527
55.0 MPa
7980 psi
ASTM D638
Elongation at Break 29.6 %
29.6 %
ISO 527
33.9 %
33.9 %
ASTM D638
Elongation at Yield 11.4 %
11.4 %
ISO 527
Tensile Modulus 2.62 GPa
380 ksi
1 mm/min; ISO 527
2.75 GPa
399 ksi
50 mm/min; ASTM D638
Flexural Strength 13.0 MPa
1890 psi
ASTM D790
70.0 MPa
10200 psi
ISO 178
Flexural Modulus 2.00 GPa
290 ksi
ISO 178
3.44 GPa
499 ksi
ASTM D790
Izod Impact, Notched 0.0500 J/cm
0.0937 ft-lb/in
ASTM D256
Izod Impact, Unnotched 0.640 J/cm
1.20 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 47.0 kJ/m²
22.4 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 1029 kJ/m²
489.6 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 5.00 J
3.69 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Coefficient of Friction, Dynamic 0.38
0.38
ASTM D3702 Modified
Coefficient of Friction, Static 0.17
0.17
ASTM D3702 Modified
K (wear) Factor 44.3 x 10-8 mm³/N-M
22.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 118 µm/m-°C

@Temperature -40.0 - 40.0 °C
65.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
119 µm/m-°C

@Temperature -40.0 - 40.0 °C
66.1 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 113 µm/m-°C

@Temperature -40.0 - 40.0 °C
62.8 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
113 µm/m-°C

@Temperature -40.0 - 40.0 °C
62.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 149 °C
300 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
157 °C

@Thickness 3.20 mm
315 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 96.0 °C
205 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
112 °C

@Thickness 3.20 mm
234 °F

@Thickness 0.126 in
unannealed; ASTM D648