SABIC Innovative Plastics LNP LUBRICOMP KG002 Acetal Copolymer

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP KG002 Acetal Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* KG002 is a compound based on Acetal Copolymer resin containing 10% Graphite. Added feature of this material is: Wear Resistant.
Physical Properties Metric English Comments
Density 1.45 g/cc
0.0524 lb/in³
ASTM D792
1.45 g/cc
0.0524 lb/in³
ISO 1183
Moisture Absorption 0.200 %
0.200 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.023 cm/cm

@Time 86400 sec
0.023 in/in

@Time 24.0 hour
ASTM D955
0.023 cm/cm

@Time 86400 sec
0.023 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.022 cm/cm

@Time 86400 sec
0.022 in/in

@Time 24.0 hour
ASTM D955
0.022 cm/cm

@Time 86400 sec
0.022 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 48.0 MPa
6960 psi
ASTM D638
49.0 MPa
7110 psi
ISO 527
Tensile Strength, Yield 51.0 MPa
7400 psi
ASTM D638
51.0 MPa
7400 psi
ISO 527
Elongation at Break 19.4 %
19.4 %
ISO 527
20.1 %
20.1 %
ASTM D638
Elongation at Yield 6.9 %
6.9 %
ASTM D638
7.5 %
7.5 %
ISO 527
Tensile Modulus 3.18 GPa
461 ksi
1 mm/min; ISO 527
3.44 GPa
499 ksi
50 mm/min; ASTM D638
Flexural Strength 70.0 MPa
10200 psi
ISO 178
Flexural Modulus 2.75 GPa
399 ksi
ASTM D790
3.00 GPa
435 ksi
ISO 178
Izod Impact, Notched 0.0500 J/cm
0.0937 ft-lb/in
ASTM D256
Izod Impact, Unnotched 0.480 J/cm
0.899 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 46.0 kJ/m²
21.9 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 692 kJ/m²
329 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 5.00 J
3.69 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.56
0.56
ASTM D3702 Modified
Coefficient of Friction, Static 0.44
0.44
ASTM D3702 Modified
K (wear) Factor 207 x 10-8 mm³/N-M
103 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 106 µm/m-°C

@Temperature -40.0 - 40.0 °C
58.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
106 µm/m-°C

@Temperature -40.0 - 40.0 °C
58.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 95.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
53.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
96.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
53.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
157 °C

@Thickness 3.20 mm
315 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
103 °C

@Thickness 3.20 mm
217 °F

@Thickness 0.126 in
unannealed; ASTM D648