Polymer Property : High Load Melt Index = 8.5 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
High Load Melt Index	8.5 g/10 min @Load 21.6 kg, Temperature 190 Â°C	8.5 g/10 min @Load 47.6 lb, Temperature 374 Â°F	ASTM D1238
Ineos TUB 121N HDPE TUB121N is a natural high density bimodal polyethylene copolymer designed for extrusion of potable water, natural gas, industrial, and mining pipe. When blended with an approved black concentrate, t..
High Load Melt Index	8.5 g/10 min @Load 21.6 kg, Temperature 190 °C	8.5 g/10 min @Load 47.6 lb, Temperature 374 °F	ISO 1133
Borealis BorPEX™ HE2590 High Density Polyethylene Compound for Crosslinked Pipes (Pex-C (Irradiation)) BorPEX HE2590 is a high molecular weight, high density polyethylene compound for crosslinkable pipes, especially designed for electron beam irradiation crosslinking. The stabilization is optimized ..
High Load Melt Index	8.5 g/10 min @Load 21.6 kg, Temperature 190 °C	8.5 g/10 min @Load 47.6 lb, Temperature 374 °F	Condition F; ASTM D1238
Formosa Plastics Formolene® E900 Pipe HDPE High Density Polyethylene High Molecular Weight Bi-Modal Resin for Non-Pressure Pipe Extrusion Applications Formolene® E900 is a high molecular weight high density polyethylene (HMW-HDPE) resin des..
High Load Melt Index	8.5 g/10 min @Load 21.6 kg, Temperature 190 °C	8.5 g/10 min @Load 47.6 lb, Temperature 374 °F	Condition F; ASTM D1238
Formosa Plastics Formolene® E924 Film HDPE High Molecular Weight High Density Polyethylene (HMW-HDPE) for Film Extrusion Formolene® E924 is a bi-modal HMW-HDPE resin designed for high dart impact strength and good processing characteristics..
High Load Melt Index	8.5 g/10 min @Load 21.6 kg, Temperature 190 °C	8.5 g/10 min @Load 47.6 lb, Temperature 374 °F	ASTM D1238
Dow CONTINUUM™ DGDC-2480 NT Bimodal Polyethylene Resin CONTINUUM™ DGDA-2490 NT is produced using UNIPOL™ II process technology. This product may be utilized for pipe applications where long term hydrostatic strength combined with outstanding resistan..
High Load Melt Index	8.5 g/10 min @Load 21.6 kg, Temperature 190 °C	8.5 g/10 min @Load 47.6 lb, Temperature 374 °F	Condition F; ASTM D1238
Formosa Plastics Formolene® E924F Film HDPE High Density Polyethylene High Molecular Weight Bi-Modal Resin for Film Applications Formolene® E924F is a “low gel” high molecular weight grade of HDPE designed for high dart impact strength and..
High Load Melt Index	8.5 g/10 min @Load 21.6 kg, Temperature 190 °C	8.5 g/10 min @Load 47.6 lb, Temperature 374 °F	ASTM D1238
Braskem HF 0147 HDPE Blown Film Extrusion Polyethylene 38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Grocery and T-shirt bags; merchandise bags; frozen-food bags. Information provided by Bras..