Covestro Makrolon® GF9002* Polycarbonate, 10% Glass Filled

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled
Manufacturer	Covestro
Trade Name	Makrolon®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Covestro Makrolon® GF9002* Polycarbonate, 10% Glass Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

ISO 7391-PC,MFR,(,,)-18-9,GF10Formerly Makrolon DP1-1889MVR (300 °C/1.2 kg) 15 cm3/10 min10 % Glass fiber reinforcedChlorine- and bromine-free flame retardantUL 94V-0/1.2 mmUL 94 5VA/2.8 mm (Bayer measurement)Low viscosityEasy releaseInjection molding - Melt temperature 310 - 330 °CAvailable in opaque colors onlyElectrical/electronicHousing parts with low wall thicknessAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.

Physical Properties	Metric	English	Comments
Density	1.27 g/cc	0.0459 lb/in³	ISO 1183
	1.08 g/cc @Temperature 300 °C	0.0390 lb/in³ @Temperature 572 °F	Melt
Water Absorption	0.26 %	0.26 %	Similar to ISO 62
Moisture Absorption at Equilibrium	0.10 %	0.10 %	Similar to ISO 62
Melt Flow	16 g/10 min @Load 1.20 kg, Temperature 300 °C	16 g/10 min @Load 2.65 lb, Temperature 572 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	45.0 MPa	6530 psi	ISO 527-1/-2
Elongation at Break	10 %	10 %	ISO 527-1/-2
Tensile Modulus	3.80 GPa	551 ksi	ISO 527-1/-2

Thermal Properties	Metric	English	Comments
Specific Heat Capacity	1.60 J/g-°C	0.382 BTU/lb-°F	Melt
Thermal Conductivity	0.191 W/m-K	1.33 BTU-in/hr-ft²-°F	Melt
Vicat Softening Point	143 °C	289 °F	50°C/h 50N; ISO 306
Flammability, UL94	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	IEC 60695-11-10
	V-0 @Thickness 1.20 mm	V-0 @Thickness 0.0472 in	IEC 60695-11-10
	5VA @Thickness 3.00 mm	5VA @Thickness 0.118 in	IEC 60695-11-20
Oxygen Index	35 %	35 %	ISO 4589-1/-2

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm	IEC 60093
Comparative Tracking Index	175 V	175 V	IEC 60112

Processing Properties	Metric	English	Comments
Melt Temperature	300 °C	572 °F	Injection Molding; ISO 294
	310 - 330 °C	590 - 626 °F
Mold Temperature	80.0 - 130 °C	176 - 266 °F
	110 °C	230 °F	Injection Molding; ISO 10724
Ejection Temperature	140 °C	284 °F
Injection Velocity	200 mm/sec	7.87 in/sec	ISO 294

Descriptive Properties	Value	Comments
Availability	Asia Pacific
	Europe
	Near East/Africa
	North America
	South and Central America
Eff. thermal diffusivity (m²/s)	1.11E-07
Feature	Release agent
Form	Pellets
Process	Injection Molding