Polymer Property : Melt Flow = 0.34 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Flow	0.34 g/10 min @Load 2.16 kg, Temperature 190 °C	0.34 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
NOVA Chemicals Sclair® 56B4 HDPE Blow Molding Resin Extra-high stress crack resistance, Good processabilityApplications: Very high ESCR, Ideally suited for use in most food, pharmaceutical, households and industrial chemical applications, Little/no s..
Melt Flow	0.34 g/10 min	0.34 g/10 min	Condition E; ASTM D 1238
Chevron Phillips HiD® 9650 HDPE Blown Film Resin (discontinued **) Resin Type: Linear Polyethylene CopolymerCharacteristics: Copolymerization Enhances Film Toughness, Excellent Film Drawdown, Unique Molecular Architecture Gives Moisture Barrier Properties Typical o..
Melt Flow	0.34 - 0.56 g/10 min @Load 5.00 kg, Temperature 190 Â°C	0.34 - 0.56 g/10 min @Load 11.0 lb, Temperature 374 Â°F	ASTM D1238-00
Ipiranga Petrochem GM 5010 T2 HDPE IPQ produces High Density Polyethylene (HDPE) for use by different segments of the plastics molding industry in several processes, including blow molding, extrusion and injection molding.To produce ..
Melt Flow	0.34 - 0.56 g/10 min @Load 5.00 kg, Temperature 190 Â°C	0.34 - 0.56 g/10 min @Load 11.0 lb, Temperature 374 Â°F	ASTM D1238-00
Ipiranga Petrochem GM 9245 F HDPE IPQ produces High Density Polyethylene (HDPE) for use by different segments of the plastics molding industry in several processes, including blow molding, extrusion and injection molding.To produce ..
Melt Flow	0.34 g/10 min @Load 2.16 kg, Temperature 190 °C	0.34 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Chevron Phillips Marlex® 9505H High Density Polyethylene This gas phase, high molecular weight, hexene copolymer with antistatic agent is tailored for lightweight blow molded containers that:Require outstanding ESCRRequire excellent impact resistanceAre d..
Melt Flow	0.34 g/10 min @Load 2.16 kg, Temperature 190 °C	0.34 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Chevron Phillips Marlex® 9509HF High Density Polyethylene, Blow Molding This gas phase, high molecular weight, hexane copolymer with synthetic antistatic agent is tailored for lightweight blow molded applications that:Require outstanding ESCRRequire excellent impact res..
Melt Flow	0.34 g/10 min @Load 2.16 kg, Temperature 190 °C	0.34 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Chevron Phillips Marlex® 9519H High Density Polyethylene, Blow Molding This gas phase, high molecular weight, homopolymer with antistatic agent is tailored for lightweight blow molded applications that:Require excellent stiffness to ESCR ratioRequire good melt strength..
Melt Flow	0.34 g/10 min @Load 2.16 kg, Temperature 190 °C	0.34 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM-D1238
Braskem LD7000A LDPE Blown Film Extrusion Polyethylene LD7000A is a low-density polyethylene produced by the high pressure process in an autoclave reactor. It is developed for the manufacturing of extruded films. It has high mechanical and impact streng..
Melt Flow	0.34 g/10 min @Load 5.00 kg, Temperature 190 °C	0.34 g/10 min @Load 11.0 lb, Temperature 374 °F
Total Finathene® 4344 HDPE, blow molding (discontinued **) Applications: storage tank liners, intermediate bulk containers, general large-part blow molding. Blow Molding Stock Temperature 370 – 410 ºFInformation provided provided by Total Petrochemicals.T..
Melt Flow	0.34 g/10 min @Load 2.16 kg, Temperature 190 °C	0.34 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Chevron Phillips Marlex® 9515H High Density Polyethylene, Blow Molding This gas phase, high molecular weight, hexane copolymer with antistatic agent is tailored for lightweight blow molded applications that:Require excellent stiffness to ESCR ratioRequire good melt str..
Melt Flow	0.34 g/10 min	0.34 g/10 min	ASTM D1238
LyondellBasell Alathon® L4434 High Density Polyethylene ApplicationsALATHON L 4434 is a medium molecular weight high density copolymer for use in blown film applications. Typical applications include blown film over pouches. Regulatory StatusL 4434 meet..
Melt Flow	0.34 g/10 min @Load 2.16 kg, Temperature 190 °C	0.34 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Chevron Phillips Marlex® 9518H High Density Polyethylene, Blow Molding This gas phase, high molecular weight, homopolymer is tailored for lightweight blow molded applications that:Require excellent stiffness to ESCR ratioRequire good melt strengthAre durable and recycl..