Polymer Property : Melt Index of Compound = 1.9 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Index of Compound	1.9 g/10 min @Load 2.16 kg, Temperature 190 °C	1.9 g/10 min @Load 4.76 lb, Temperature 374 °F	cm3/10 min; ISO 1133
DuPont Performance Polymers Delrin® 150 NC010 Acetal Homopolymer (Unverified Data**) Delrin® 150 NC010 is a high viscosity acetal homopolymer for extrusion processes. It has excellent thermal stability, low die deposit, and enhanced crystallization for low porosity.Information pr..
Melt Index of Compound	1.9 g/10 min @Load 2.16 kg, Temperature 230 °C	1.9 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
Dow 359.00 Developmental Performance Polypropylene Polymer Dow Announced Sale of Global Polypropylene Business to Braskem in July 2011.
Melt Index of Compound	1.9 g/10 min @Load 2.16 kg, Temperature 230 °C	1.9 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
Dow 6D20 Polypropylene Random Copolymer Resin OverviewConsistent processabilityGood regrind stabilityGood gloss and clarityLow odor and taste transferComplies with: U.S. FDA 21 CFR 177.1520 (c)3.1a, Europe EU-Directive 2002/72/ECDOW 6D20 Polypr..
Melt Index of Compound	1.9 g/10 min @Load 2.16 kg, Temperature 230 °C	1.9 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
Dow 6D83K Polypropylene Random Copolymer Resin OverviewConsistent processabilityLow odor and taste transferHigh glossGood regrind stabilityContains clarifying additiveComplies with: U.S. FDA 21 CFR 177.1520 (c)3.2a, Canadian HPFB No ObjectionDOW..
Melt Index of Compound	1.9 g/10 min @Load 2.16 kg, Temperature 230 °C	1.9 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
Dow C133-02 Polypropylene Impact Copolymer Resin OverviewDow C133-02 Polypropylene Resin is intended for use in extrusion, thermoforming, and extrusion blow molding applications where impact at refrigeration temperatures is desired. It is especia..
Melt Index of Compound	1.9 g/10 min @Load 2.16 kg, Temperature 230 °C	1.9 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
Dow R131-02A Polypropylene Random Copolymer Resin DOW R131-02A Polypropylene Resin is a random copolymer intended for use in extrusion blow molding applications. The product can be used in both single layer and multilayer designs including barrier..
Melt Index of Compound	1.9 g/10 min @Load 2.16 kg, Temperature 190 °C	1.9 g/10 min @Load 4.76 lb, Temperature 374 °F	cm3/10 min; ISO 1133
DuPont Performance Polymers Delrin® 111P NC010 Acetal Homopolymer Delrin® 111P is a high viscosity acetal homopolymer with improved thermal stability and modifications for more precise molding (reduced warpage, fewer voids). It has higher tensile strength and mod..
Melt Index of Compound	1.9 g/10 min @Load 2.16 kg, Temperature 230 °C	1.9 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
Dow R132-02A Polypropylene Random Copolymer Resin DOW R132-02A Polypropylene Resin is a random copolymer intended for use in extrusion blow molding applications. The product can be used in both single layer and multilayer designs including barrier..
Melt Index of Compound	1.9 g/10 min @Load 2.16 kg, Temperature 190 °C	1.9 g/10 min @Load 4.76 lb, Temperature 374 °F	cm3/10 min; ISO 1133
DuPont Performance Polymers Delrin® FG150 NC010 Acetal Homopolymer (Unverified Data**) Delrin® FG150 NC010 is a high viscosity acetal homopolymer for extrusion processes. It has low die deposit and low porosity. It has been developed for consideration in applications and parts for th..
Melt Index of Compound	1.9 g/10 min @Load 2.16 kg, Temperature 190 °C	1.9 g/10 min @Load 4.76 lb, Temperature 374 °F	cm3/10 min; ISO 1133
DuPont Performance Polymers Delrin® FG100P NC010 Acetal Homopolymer (Unverified Data**) Delrin® FG100P is a high viscosity acetal homopolymer, with improved thermal stability for use in easy to fill molds. It has been developed for consideration into applications such as parts for the..