Material Notes:

Delrin® FG100P is a high viscosity acetal homopolymer, with improved thermal stability for use in easy to fill molds. It has been developed for consideration into applications such as parts for the food industry.Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.42 g/cc	0.0513 lb/in³	ISO 1183
Water Absorption	0.30 % @Temperature 23.0 °C	0.30 % @Temperature 73.4 °F	Equilibrium 50%RH; ISO 62, Similar to
	1.4 % @Temperature 23.0 °C	1.4 % @Temperature 73.4 °F	Saturation, immersed; ISO 62, Similar to
Linear Mold Shrinkage, Flow	0.022 cm/cm @Thickness 2.00 mm	0.022 in/in @Thickness 0.0787 in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.020 cm/cm @Thickness 2.00 mm	0.020 in/in @Thickness 0.0787 in	ISO 294-4
Melt Flow	2.5 g/10 min @Load 2.16 kg, Temperature 190 °C	2.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Melt Index of Compound	1.9 g/10 min @Load 2.16 kg, Temperature 190 °C	1.9 g/10 min @Load 4.76 lb, Temperature 374 °F	cm3/10 min; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	70.0 MPa @Temperature 23.0 °C	10200 psi @Temperature 73.4 °F	ISO 527
Elongation at Break	45 % @Temperature 23.0 °C	45 % @Temperature 73.4 °F	nominal; ISO 527
Elongation at Yield	25 % @Temperature 23.0 °C	25 % @Temperature 73.4 °F	ISO 527
Tensile Modulus	2.90 GPa @Temperature 23.0 °C	421 ksi @Temperature 73.4 °F	ISO 527
Flexural Modulus	2.60 GPa @Temperature 23.0 °C	377 ksi @Temperature 73.4 °F	ISO 178
Charpy Impact Unnotched	35.0 J/cm² @Temperature -30.0 °C	167 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	1.10 J/cm² @Temperature -30.0 °C	5.23 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	1.40 J/cm² @Temperature 23.0 °C	6.66 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA
Tensile Creep Modulus, 1 hour	2700 MPa @Temperature 23.0 °C	392000 psi @Temperature 73.4 °F	ISO 899
Tensile Creep Modulus, 1000 hours	1500 MPa @Temperature 23.0 °C	218000 psi @Temperature 73.4 °F	ISO 899

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	500 µm/m-°C @Temperature -40.0 - 23.0 °C	278 µin/in-°F @Temperature -40.0 - 73.4 °F	ISO 11359-1/-2
	500 µm/m-°C @Temperature 23.0 - 55.0 °C	278 µin/in-°F @Temperature 73.4 - 131 °F	ISO 11359-1/-2
	500 µm/m-°C @Temperature 55.0 - 100 °C	278 µin/in-°F @Temperature 131 - 212 °F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	100 µm/m-°C @Temperature -40.0 - 23.0 °C	55.6 µin/in-°F @Temperature -40.0 - 73.4 °F	ISO 11359-1/-2
	110 µm/m-°C @Temperature 23.0 - 55.0 °C	61.1 µin/in-°F @Temperature 73.4 - 131 °F	ISO 11359-1/-2
	150 µm/m-°C @Temperature 55.0 - 100 °C	83.3 µin/in-°F @Temperature 131 - 212 °F	ISO 11359-1/-2
Melting Point	178 °C	352 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	160 °C	320 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	93.0 °C	199 °F	ISO 75-1/-2

Processing Properties	Metric	English	Comments
Melt Temperature	215 °C	419 °F	Optimum; Injection Molding
	210 - 220 °C	410 - 428 °F	Injection Molding
Mold Temperature	90.0 °C	194 °F	optimum; Injection Molding
	80.0 - 100 °C	176 - 212 °F	Injection Molding
Drying Temperature	80.0 °C	176 °F	Injection Molding
Dry Time	2.00 - 4.00 hour	2.00 - 4.00 hour	Injection Molding
Moisture Content	<= 0.20 %	<= 0.20 %	Injection Molding

Descriptive Properties	Value	Comments
Appearance	Natural Color
Features	Creep Resistance, Good
	Dimensional Stability, Good
	Fatigue Resistant
	Homopolymer
	Impact Resistance, High
	Molecular Wt., High
	Stiffness, High
	Strength, High
	Toughness, Good
	Viscosity, High
Forms	Pellets
Generic	Acetal (POM) Homopolymer
Material Status	Preliminary Data
Part Marking Code	>POM<	ISO 11469
Processing Method	Injection Molding
Product Category	Food Contact Resins
	Unreinforced Resins
Region Available - Global	Yes
Resin Identification	POM	ISO 1043
RoHS Compliance	Contact Manufacturer
Uses	Conveyors
	Fasteners
	Food Applications, Non-specific
	Gears
	Housings
	Parts, Engineering
	Sheet
	Tubing