DuPont Performance Polymers Delrin® FG150 NC010 Acetal Homopolymer (Unverified Data**)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Delrin® FG150 NC010 Acetal Homopolymer
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Delrin® FG150 NC010 is a high viscosity acetal homopolymer for extrusion processes. It has low die deposit and low porosity. It has been developed for consideration in applications and parts for the food industryInformation provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Water Absorption | 0.39 % @Temperature 23.0 °C |
0.39 % @Temperature 73.4 °F |
Immersion 24h; ISO 62, Similar to |
| Linear Mold Shrinkage, Flow | 0.018 cm/cm @Thickness 2.00 mm |
0.018 in/in @Thickness 0.0787 in |
ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.020 cm/cm @Thickness 2.00 mm |
0.020 in/in @Thickness 0.0787 in |
ISO 294-4 |
| Melt Flow | 2.4 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.4 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Melt Index of Compound | 1.9 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.9 g/10 min @Load 4.76 lb, Temperature 374 °F |
cm3/10 min; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 72.0 MPa @Temperature 23.0 °C |
10400 psi @Temperature 73.4 °F |
ISO 527 |
| Elongation at Break | 40 % @Temperature 23.0 °C |
40 % @Temperature 73.4 °F |
nominal; ISO 527 |
| Elongation at Yield | 22 % @Temperature 23.0 °C |
22 % @Temperature 73.4 °F |
ISO 527 |
| Tensile Modulus | 3.10 GPa @Temperature 23.0 °C |
450 ksi @Temperature 73.4 °F |
ISO 527 |
| Flexural Modulus | 2.90 GPa @Temperature 23.0 °C |
421 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature -40.0 - 23.0 °C |
278 µin/in-°F @Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2 |
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1/-2 | |
| 500 µm/m-°C @Temperature 55.0 - 100 °C |
278 µin/in-°F @Temperature 131 - 212 °F |
ISO 11359-1/-2 | |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
50.0 µin/in-°F @Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2 |
| 100 µm/m-°C @Temperature 23.0 - 55.0 °C |
55.6 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1/-2 | |
| 150 µm/m-°C @Temperature 55.0 - 100 °C |
83.3 µin/in-°F @Temperature 131 - 212 °F |
ISO 11359-1/-2 | |
| Melting Point | 178 °C | 352 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | ISO 75-1/-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 195 - 205 °C | 383 - 401 °F | Extrusion |
| 200 °C | 392 °F | Optimum; Extrusion | |
| 215 °C | 419 °F | Optimum; Injection Molding | |
| 210 - 220 °C | 410 - 428 °F | Injection Molding | |
| Mold Temperature | 90.0 °C | 194 °F | optimum; Injection Molding |
| 80.0 - 100 °C | 176 - 212 °F | Injection Molding | |
| Drying Temperature | 80.0 °C | 176 °F | Injection Molding |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Injection Molding |
| Moisture Content | <= 0.20 % | <= 0.20 % | Extrusion |
| <= 0.20 % | <= 0.20 % | Injection Molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Natural Color | |
| Features | Creep Resistance, Good | |
| Dimensional Stability, Good | ||
| Fatigue Resistant | ||
| Homopolymer | ||
| Impact Resistance, High | ||
| Molecular Wt., High | ||
| Stiffness, High | ||
| Strength, High | ||
| Toughness, Good | ||
| Viscosity, High | ||
| Forms | Pellets | |
| Generic | Acetal (POM) Homopolymer | |
| Material Status | Preliminary Data | |
| Part Marking Code | >POM< | ISO 11469 |
| Processing Method | Injection Molding | |
| Product Category | Extrusion Resins | |
| Extrusion Resins | ||
| Food Contact Resins | ||
| Unreinforced Resins | ||
| Region Available - Global | Yes | |
| Resin Identification | POM | ISO 1043 |
| RoHS Compliance | Contact Manufacturer | |
| Uses | Food Applications, Non-specific | |
| Parts, Engineering | ||
| Sheet | ||
| Tubing |