Borealis Xmod™ GB306SAF Polypropylene, Glass Fiber Reinforced

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Glass Fiber Filler
Manufacturer	Borealis
Trade Name	Xmod™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Borealis Xmod™ GB306SAF Polypropylene, Glass Fiber Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Xmod™ GB306SAF is a 35 % chemically coupled high performance glass fiber reinforced polypropylene compound intended for injection molding. The product is available in standard black 9502. This material shows excellent mechanical properties also at elevated temperatures. Applications: Xmod™ GB306SAF has been developed especially for demanding applications in under the bonnet applications, air intake manifolds, parts for cooling systems, fans and shrouds, and technical components exposed to high heat and loads.Information provided by Borealis AG

Physical Properties	Metric	English	Comments
Density	1.18 g/cc	0.0426 lb/in³	ISO 1183
Linear Mold Shrinkage	0.0010 - 0.0020 cm/cm	0.0010 - 0.0020 in/in	average process; in flow; 150x80x2mm
	0.0080 - 0.012 cm/cm	0.0080 - 0.012 in/in	average process; cross flow; 150x80x2mm
Melt Flow	2.0 g/10 min @Load 2.16 kg, Temperature 230 °C	2.0 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	118 MPa	17100 psi	ISO 527-2
Elongation at Break	2.8 %	2.8 %	50mm/min; ISO 527-2
Tensile Modulus	9.00 GPa	1310 ksi	1mm/min; ISO 527-2
Flexural Strength	170 MPa	24700 psi	ISO 178
Flexural Modulus	8.00 GPa	1160 ksi	2mm/min; ISO 178
Izod Impact, Notched (ISO)	10.0 kJ/m² @Temperature -20.0 °C	4.76 ft-lb/in² @Temperature -4.00 °F	ISO 180/1A
	11.0 kJ/m² @Temperature 23.0 °C	5.23 ft-lb/in² @Temperature 73.4 °F	ISO 180/1A
Charpy Impact Unnotched	5.40 J/cm² @Temperature -20.0 °C	25.7 ft-lb/in² @Temperature -4.00 °F	ISO 179/1eU
	5.80 J/cm² @Temperature 23.0 °C	27.6 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	1.00 J/cm² @Temperature -30.0 °C	4.76 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	1.10 J/cm² @Temperature 23.0 °C	5.23 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	154 °C	309 °F	ISO 75-2
Vicat Softening Point	142 °C @Load 5.10 kg	288 °F @Load 11.2 lb	ISO 306

Processing Properties	Metric	English	Comments
Processing Temperature	230 - 280 °C	446 - 536 °F	mass temperature
Feed Temperature	40.0 - 80.0 °C	104 - 176 °F
Mold Temperature	30.0 - 50.0 °C	86.0 - 122 °F
Injection Velocity	1667 - 3333 mm/sec	65.63 - 131.2 in/sec
Hold Pressure	30.0 - 60.0 MPa	4350 - 8700 psi

Descriptive Properties	Value	Comments
Back Pressure	low to medium
Screw Speed	low to medium