DuPont Performance Polymers Zytel® 80G33HS1L NC010 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 80G33HS1L NC010 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
33% Glass Reinforced Toughened Heat Stabilized Polyamide 66 Zytel 80G33HS1L NC010 is a 33% glass fiber reinforced heat stabilized polyamide 66 resin with outstanding impact resistance developed using DuPont Super Tough technology.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.12 g/cc
0.0405 lb/in³
1.33 g/cc
0.0480 lb/in³
DAM; ISO 1183
Water Absorption 4.5 %

@Thickness 2.00 mm
 4.5 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 1.50 %

@Thickness 2.00 mm
 1.50 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Water Absorption at Saturation 0.85 %
0.85 %
DAM; Immersion 24h; ASTM D570
Viscosity 69805 cP

@Shear Rate 5000 1/s,
Temperature 305 °C
 69805 cP

@Shear Rate 5000 1/s,
Temperature 581 °F
 ISO 11403-1 -2
88510 cP

@Shear Rate 5000 1/s,
Temperature 295 °C
 88510 cP

@Shear Rate 5000 1/s,
Temperature 563 °F
 ISO 11403-1 -2
115100 cP

@Shear Rate 5000 1/s,
Temperature 285 °C
 115100 cP

@Shear Rate 5000 1/s,
Temperature 545 °F
 ISO 11403-1 -2
241800 cP

@Shear Rate 500 1/s,
Temperature 305 °C
 241800 cP

@Shear Rate 500 1/s,
Temperature 581 °F
 ISO 11403-1 -2
308700 cP

@Shear Rate 500 1/s,
Temperature 295 °C
 308700 cP

@Shear Rate 500 1/s,
Temperature 563 °F
 ISO 11403-1 -2
403200 cP

@Shear Rate 500 1/s,
Temperature 285 °C
 403200 cP

@Shear Rate 500 1/s,
Temperature 545 °F
 ISO 11403-1 -2
Viscosity Test 160 cm³/g
160 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Hardness, Rockwell M 70
70
DAM; ISO 2039-2
Hardness, Rockwell R 110
110
DAM; ISO 2039-2
Tensile Strength at Break 108 MPa
15700 psi
50%RH; ISO 527-1/-2
146 MPa
21200 psi
DAM; ISO 527-1/-2
Tensile Stress 8.47 MPa

@Strain 0.230 %,
Temperature 150 °C
 1230 psi

@Strain 0.230 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
10.7 MPa

@Strain 0.240 %,
Temperature 90.0 °C
 1550 psi

@Strain 0.240 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
11.24 MPa

@Strain 0.240 %,
Temperature 90.0 °C
 1630 psi

@Strain 0.240 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
13.42 MPa

@Strain 0.420 %,
Temperature 150 °C
 1946 psi

@Strain 0.420 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
19.37 MPa

@Strain 0.330 %,
Temperature 40.0 °C
 2809 psi

@Strain 0.330 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
26.06 MPa

@Strain 0.820 %,
Temperature 150 °C
 3780 psi

@Strain 0.820 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
30.98 MPa

@Strain 1.24 %,
Temperature 150 °C
 4493 psi

@Strain 1.24 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
31.49 MPa

@Strain 0.830 %,
Temperature 90.0 °C
 4567 psi

@Strain 0.830 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
34.96 MPa

@Strain 0.310 %,
Temperature -40.0 °C
 5071 psi

@Strain 0.310 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
36.33 MPa

@Strain 0.890 %,
Temperature 90.0 °C
 5269 psi

@Strain 0.890 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
41.33 MPa

@Strain 0.590 %,
Temperature 23.0 °C
 5994 psi

@Strain 0.590 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
44.4 MPa

@Strain 2.51 %,
Temperature 150 °C
 6440 psi

@Strain 2.51 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
44.82 MPa

@Strain 0.510 %,
Temperature 40.0 °C
 6501 psi

@Strain 0.510 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
45.52 MPa

@Strain 1.99 %,
Temperature 150 °C
 6602 psi

@Strain 1.99 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
51.14 MPa

@Strain 1.03 %,
Temperature 40.0 °C
 7417 psi

@Strain 1.03 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
53.18 MPa

@Strain 4.05 %,
Temperature 150 °C
 7713 psi

@Strain 4.05 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
53.24 MPa

@Strain 1.88 %,
Temperature 90.0 °C
 7722 psi

@Strain 1.88 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
58.28 MPa

@Strain 3.57 %,
Temperature 150 °C
 8453 psi

@Strain 3.57 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
59.6 MPa

@Strain 0.710 %,
Temperature 0.000 °C
 8640 psi

@Strain 0.710 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
62.58 MPa

@Strain 1.99 %,
Temperature 90.0 °C
 9076 psi

@Strain 1.99 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
67.95 MPa

@Strain 3.35 %,
Temperature 90.0 °C
 9855 psi

@Strain 3.35 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
69.02 MPa

@Strain 0.760 %,
Temperature 23.0 °C
 10010 psi

@Strain 0.760 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
69.98 MPa

@Strain 0.740 %,
Temperature -20.0 °C
 10150 psi

@Strain 0.740 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
76.42 MPa

@Strain 1.31 %,
Temperature 23.0 °C
 11080 psi

@Strain 1.31 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
79.23 MPa

@Strain 2.10 %,
Temperature 40.0 °C
 11490 psi

@Strain 2.10 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
81.91 MPa

@Strain 3.42 %,
Temperature 90.0 °C
 11880 psi

@Strain 3.42 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
88.29 MPa

@Strain 0.870 %,
Temperature -40.0 °C
 12810 psi

@Strain 0.870 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
90.52 MPa

@Strain 1.19 %,
Temperature 40.0 °C
 13130 psi

@Strain 1.19 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
90.65 MPa

@Strain 0.980 %,
Temperature 0.000 °C
 13150 psi

@Strain 0.980 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
96.81 MPa

@Strain 3.55 %,
Temperature 40.0 °C
 14040 psi

@Strain 3.55 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
100.09 MPa

@Strain 1.07 %,
Temperature -40.0 °C
 14517 psi

@Strain 1.07 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
100.58 MPa

@Strain 1.35 %,
Temperature 0.000 °C
 14588 psi

@Strain 1.35 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
104.57 MPa

@Strain 2.27 %,
Temperature 23.0 °C
 15167 psi

@Strain 2.27 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
105.95 MPa

@Strain 1.16 %,
Temperature -20.0 °C
 15367 psi

@Strain 1.16 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
114.59 MPa

@Strain 1.47 %,
Temperature 23.0 °C
 16620 psi

@Strain 1.47 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
115.64 MPa

@Strain 1.36 %,
Temperature -20.0 °C
 16772 psi

@Strain 1.36 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
121.49 MPa

@Strain 3.63 %,
Temperature 23.0 °C
 17621 psi

@Strain 3.63 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
127.79 MPa

@Strain 2.22 %,
Temperature 40.0 °C
 18534 psi

@Strain 2.22 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
134.54 MPa

@Strain 2.17 %,
Temperature 0.000 °C
 19513 psi

@Strain 2.17 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
140.54 MPa

@Strain 1.57 %,
Temperature -40.0 °C
 20384 psi

@Strain 1.57 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
142.15 MPa

@Strain 1.79 %,
Temperature 0.000 °C
 20617 psi

@Strain 1.79 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
143.3 MPa

@Strain 4.06 %,
Temperature 40.0 °C
 20780 psi

@Strain 4.06 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
151.92 MPa

@Strain 2.49 %,
Temperature 23.0 °C
 22034 psi

@Strain 2.49 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
153.48 MPa

@Strain 1.89 %,
Temperature -20.0 °C
 22260 psi

@Strain 1.89 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
154.85 MPa

@Strain 2.14 %,
Temperature -20.0 °C
 22459 psi

@Strain 2.14 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
157.32 MPa

@Strain 3.39 %,
Temperature 0.000 °C
 22817 psi

@Strain 3.39 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
158.08 MPa

@Strain 1.86 %,
Temperature -40.0 °C
 22928 psi

@Strain 1.86 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
181.01 MPa

@Strain 3.02 %,
Temperature 0.000 °C
 26253 psi

@Strain 3.02 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2