Samsung Cheil Industries Infino® TP-1002 PC, Unreinforced FR

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded
Manufacturer Samsung, Cheil Industries
Trade Name Infino®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Samsung Cheil Industries Infino® TP-1002 PC, Unreinforced FR.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Samsung Cheil Industries.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 30 g/10 min

@Load 10.0 kg,
Temperature 250 °C
 30 g/10 min

@Load 22.0 lb,
Temperature 482 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ASTM D785
Tensile Strength at Break 68.6 MPa
9950 psi
50 mm/min; ASTM D638
Tensile Strength, Yield 58.8 MPa
8530 psi
50 mm/min; ASTM D638
Elongation at Break 114 %
114 %
50 mm/min; ASTM D638
Tensile Modulus 1.96 GPa
284 ksi
50 mm/min; ASTM D638
Flexural Strength 88.3 MPa
12800 psi
2.8 mm/min; ASTM D790
Flexural Modulus 2.26 GPa
327 ksi
2.8 mm/min; ASTM D790
Izod Impact, Notched 0.951 J/cm

@Thickness 6.35 mm
 1.78 ft-lb/in

@Thickness 0.250 in
 ASTM D256
6.37 J/cm

@Thickness 3.17 mm
 11.9 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 142 °C

@Thickness 6.40 mm
 288 °F

@Thickness 0.252 in
 ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 130 °C

@Thickness 6.40 mm
 266 °F

@Thickness 0.252 in
 ASTM D648
Vicat Softening Point 145 °C
293 °F
B/50; ISO R306
148 °C
298 °F
B/120; ISO R306
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in