Unitika UG-100-30 Engineering Plastic
| Category | Polymer , Thermoplastic , Polyarylate |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika UG-100-30 Engineering Plastic.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent creep resistance, dimensional stability at high temperatureInformation provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ASTM D792 |
| Water Absorption | 0.24 % @Thickness 3.17 mm, Time 86400 sec |
0.24 % @Thickness 0.125 in, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0055 cm/cm @Thickness 3.00 mm |
0.0055 in/in @Thickness 0.118 in |
|
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Thickness 3.00 mm |
0.0030 - 0.0050 in/in @Thickness 0.118 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength at Break | 132 MPa | 19100 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| Flexural Strength | 133 MPa | 19300 psi | ASTM D790 |
| Flexural Modulus | 5.70 GPa | 827 ksi | ASTM D790 |
| Izod Impact, Notched | 1.00 J/cm @Thickness 3.17 mm |
1.87 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 35.0 µm/m-°C | 19.4 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.60e+14 ohm-cm | 4.60e+14 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | ASTM D149 |
| Dissipation Factor | 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 310 - 330 °C | 590 - 626 °F | |
| Middle Barrel Temperature | 340 - 360 °C | 644 - 680 °F | |
| Front Barrel Temperature | 350 - 370 °C | 662 - 698 °F | |
| Nozzle Temperature | 350 - 370 °C | 662 - 698 °F | |
| Mold Temperature | 120 - 140 °C | 248 - 284 °F | actual surface temp |
| Drying Temperature | 140 °C | 284 °F | |
| Dry Time | 6.00 - 24.0 hour | 6.00 - 24.0 hour | |
| Back Pressure | 0.490 - 1.47 MPa | 71.1 - 213 psi | gage pressure |
Users viewing this material also viewed the following:
- PolyOne Edgetek® RA-10GF-10CF/000 HI Polyphenylsulfone (PPSU)
- Polimeri Europa KOBLEND HI PD 41 G1 PBT+PC, 5% Glass Fiber (discontinued **)
- PolyOne Geon™ Vinyl Flexible B550B Polyvinyl Chloride, Flexible (PVC, Flexible)
- Sylvin Technologies 9940-60 Natural PVC Molding Compound
- Samsung Cheil Industries Infino® LB-1010W PC, Unreinforced FR
- Cheng Yu Plastic N66C3 Nylon 66, 30% Mineral Reinforced
- Azoty Tarnow™ Tarnamid® T-27 GF30 TF15 Polyamide 6 - Improved Slip Properties
- ATI Allegheny Ludlum Stainless Steel Type 321 (UNS S32100)
Copyright © lookpolymers.com All Rights Reserved