Unitika CX-2500 PA6, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika CX-2500 PA6, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Transparent nylonInformation provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ISO 1183 |
| Water Absorption | 0.70 % @Time 86400 sec |
0.70 % @Time 24.0 hour |
ISO 62 |
| Moisture Absorption at Equilibrium | 1.3 % | 1.3 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Thickness 3.20 mm |
0.0070 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm @Thickness 3.20 mm |
0.013 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 90.0 MPa | 13100 psi | ISO 527-1/-2 |
| Elongation at Break | 60 % | 60 % | ISO 527-1/-2 |
| Elongation at Yield | 6.0 % | 6.0 % | ISO 527-1/-2 |
| Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527-1/-2 |
| Flexural Strength | 126 MPa | 18300 psi | ISO 178 |
| Flexural Modulus | 2.90 GPa | 421 ksi | ISO 178 |
| Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 77.0 µm/m-°C | 42.8 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-2 @Thickness 0.750 mm |
V-2 @Thickness 0.0295 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz |
3.3 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 33.0 kV/mm @Thickness 1.00 mm |
838 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.060 @Frequency 1.00e+6 Hz |
0.060 @Frequency 1.00e+6 Hz |
IEC 60250 |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE D 5302 NAT
- Nitriflex NP-2183 Powdered Nitrile
- Omni Plastics OmniTech™ HPP TF20 V0 Flame Retardant
- Aremco Aremco-Seal™ FO-380 High Temperature Specialty Coatings Silicone, Ceramic Filled (discontinued **)
- Haynes 625 alloy, plate after 4000 hours at 760°C (1400°F)
- SABIC Innovative Plastics LNP VERTON RVL28 PA 66
- A. Schulman SCHULAMID® 66 GF33 33% Glass Fiber Reinforced Nylon 66
- Zeon Chemicals Sivic® Z2710 Polyblend Nitrile Elastomer
- Eurostar Staramide PF006S PA6, 30% Glass Fiber Filled, Injection Molded
- BASF Petra® 330 FR BK-112 30% Glass Filled PET
Copyright © lookpolymers.com All Rights Reserved