Unitika AXF-1500-05 Dry
| Category | Polymer , Thermoplastic , Polyarylate |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika AXF-1500-05 Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics: Lubricant grade of AX1500, excellent in heat and chemical resistancesInformation provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Water Absorption | 0.75 % @Thickness 3.17 mm, Time 86400 sec |
0.75 % @Thickness 0.125 in, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm @Thickness 3.00 mm |
0.010 in/in @Thickness 0.118 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength at Break | 67.0 MPa | 9720 psi | ASTM D638 |
| Elongation at Break | 15 % | 15 % | ASTM D638 |
| Flexural Strength | 100 MPa | 14500 psi | ASTM D790 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ASTM D790 |
| Compressive Strength | 82.0 MPa | 11900 psi | ASTM D695 |
| Izod Impact, Notched | 0.540 J/cm @Thickness 3.17 mm |
1.01 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 74.0 µm/m-°C | 41.1 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 210 - 230 °C | 410 - 446 °F | |
| Middle Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |
| Front Barrel Temperature | 250 - 270 °C | 482 - 518 °F | |
| Nozzle Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | actual surface temp |
| Drying Temperature | 100 °C | 212 °F | |
| Dry Time | 10.0 - 24.0 hour | 10.0 - 24.0 hour | |
| Back Pressure | 0.490 - 1.47 MPa | 71.1 - 213 psi | gage pressure |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 2005 T BLK Polypropylene
- RheTech Products G13P100-332UV 13% Glass Fiber Reinforced Polypropylene, UV Stabilized, (GM 9772) Light Neutral
- PPT LSF120 Low Sintering Temperature Ferrite Powder
- Samsung Cheil Industries Infino® VB-5302GR PBT, 30% Glass Filled FR
- Loctite® 3341 Light Cure Acrylic Adhesive
- Eurostar Starflam AFR682A1 PA66, Mineral Reinforced, Flame Retardant, Injection Molding
- 3M Filtek™ P60 Posterior Restorative Dental Composite
- 3M Scotch® 4737T High Temperature Fine Line Tape
- Loctite® Output™ 383 Acrylic Adhesive
Copyright © lookpolymers.com All Rights Reserved