LATI Later 4-V0 PBT, Flame Retardant

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Flame Retardant
Manufacturer LATI
Trade Name Later
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Later 4-V0 PBT, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polybutylene Terephthalate (PBT) based compound. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE and antimony trioxide freeAvailability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
Linear Mold Shrinkage, Flow 0.015 - 0.018 cm/cm
0.015 - 0.018 in/in
Linear Mold Shrinkage, Transverse 0.015 - 0.018 cm/cm
0.015 - 0.018 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 20.0 MPa

@Temperature 90.0 °C
 2900 psi

@Temperature 194 °F
35.0 MPa

@Temperature 60.0 °C
 5080 psi

@Temperature 140 °F
45.0 MPa

@Temperature 23.0 °C
 6530 psi

@Temperature 73.4 °F
Elongation at Break 20 %

@Temperature 23.0 °C
 20 %

@Temperature 73.4 °F
55 %

@Temperature 60.0 °C
 55 %

@Temperature 140 °F
90 %

@Temperature 90.0 °C
 90 %

@Temperature 194 °F
>= 100 %

@Temperature 120 °C
 >= 100 %

@Temperature 248 °F
>= 100 %

@Temperature 150 °C
 >= 100 %

@Temperature 302 °F
Elongation at Yield 3.0 %

@Temperature 23.0 °C
 3.0 %

@Temperature 73.4 °F
4.5 %

@Temperature 60.0 °C
 4.5 %

@Temperature 140 °F
9.0 %

@Temperature 90.0 °C
 9.0 %

@Temperature 194 °F
Tensile Modulus 0.450 GPa

@Temperature 150 °C
 65.3 ksi

@Temperature 302 °F
0.700 GPa

@Temperature 120 °C
 102 ksi

@Temperature 248 °F
1.00 GPa

@Temperature 90.0 °C
 145 ksi

@Temperature 194 °F
1.60 GPa

@Temperature 60.0 °C
 232 ksi

@Temperature 140 °F
2.80 GPa

@Temperature 23.0 °C
 406 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 2.00 J/cm²
9.52 ft-lb/in²
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 120 °C
248 °F
Deflection Temperature at 0.46 MPa (66 psi) 170 °C
338 °F
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
Vicat Softening Point 185 °C

@Load 5.00 kg
 365 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
Oxygen Index 30 %
30 %
Glow Wire Test 700 °C

@Thickness 1.00 mm
 1290 °F

@Thickness 0.0394 in
 GWIT
700 °C

@Thickness 2.00 mm
 1290 °F

@Thickness 0.0787 in
 GWIT
960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 250 V
250 V
A solution
Processing Properties Metric English Comments
Melt Temperature 230 - 240 °C
446 - 464 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 110 - 130 °C

@Time 10800 sec
 230 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa