Unitika AXF-1500-05 Conditioned
| Category | Polymer , Thermoplastic , Polyarylate |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika AXF-1500-05 Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics: Lubricant grade of AX1500, excellent in heat and chemical resistancesInformation provided by Unitika Ltd.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 54.0 MPa | 7830 psi | ASTM D638 |
| Elongation at Break | 22 % | 22 % | ASTM D638 |
| Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
| Flexural Modulus | 1.10 GPa | 160 ksi | ASTM D790 |
| Izod Impact, Notched | 1.47 J/cm @Thickness 3.17 mm |
2.75 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz |
3.6 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | ASTM D149 |
| Dissipation Factor | 0.040 @Frequency 1.00e+6 Hz |
0.040 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Arc Resistance | 80 sec | 80 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 210 - 230 °C | 410 - 446 °F | |
| Middle Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |
| Front Barrel Temperature | 250 - 270 °C | 482 - 518 °F | |
| Nozzle Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | actual surface temp |
| Drying Temperature | 100 °C | 212 °F | |
| Dry Time | 10.0 - 24.0 hour | 10.0 - 24.0 hour | |
| Back Pressure | 0.490 - 1.47 MPa | 71.1 - 213 psi | gage pressure |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 1200H-25 Fiberglass Reinforced Thermoset SMC
- NIZHNEKAMSKNEFTEKHIM PE 4118Q (18403) Linear Low Density Polyethylene
- Radici Radilon® SHS (dry) Nylon 6
- A. Schulman FORMION™ FI 226 40% Glass Fiber Reinforced Ionomer / Nylon Alloy
- Hexcel® HexWeb® CR-PAA™ 3/8-5052-0.0015 Phosphoric Acid Anodized Aluminum Honeycomb
- Chesterton 730 Spragrip®
- DSM Akulon® S223-GM35 (Cond.) 15% Glass Reinforced, 25% Mineral Reinforced Nylon 66 (North America)
- Beijing Chemical Industry KAIFA® 3030F PET Resin
- Indium Corp. 3N Commercial Indium Metal
Copyright © lookpolymers.com All Rights Reserved