SABIC Innovative Plastics LNP LUBRICOMP PFL36 PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP PFL36 PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* PFL36 is a compound based on Nylon 6 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 109 MPa | 15800 psi | ASTM D638 |
| 113 MPa | 16400 psi | ISO 527 | |
| Tensile Strength, Yield | 110 MPa | 16000 psi | ASTM D638 |
| 113 MPa | 16400 psi | ISO 527 | |
| Elongation at Break | 4.4 % | 4.4 % | ISO 527 |
| 6.7 % | 6.7 % | ASTM D638 | |
| Elongation at Yield | 4.1 % | 4.1 % | ISO 527 |
| 5.8 % | 5.8 % | ASTM D638 | |
| Tensile Modulus | 7.88 GPa | 1140 ksi | 1 mm/min; ISO 527 |
| 8.27 GPa | 1200 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 172 MPa | 24900 psi | ISO 178 |
| Flexural Modulus | 5.51 GPa | 799 ksi | ASTM D790 |
| 7.00 GPa | 1020 ksi | ISO 178 | |
| Izod Impact, Notched | 1.49 J/cm | 2.79 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.89 J/cm | 20.40 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 79.0 kJ/m² | 37.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 19.0 J | 14.0 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 421 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 216 °C @Thickness 3.20 mm |
421 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 396 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 201 °C @Thickness 3.20 mm |
394 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylon® N1040MGL Nylon 6/6 (DAM) (discontinued **)
- Karina E818-10/23-CRM White PVC Compound
- Techmer ES HiFill® ABS E GM30 LE 30% Glass Filled
- Spartech PP5420 Glass Fiber Reinforced Homopolymer
- Shinkong Synthetic Fibers Shinite® T101G45 PET, 45% Glass Filled
- Sax Polymers SAXAMID 226F6 Nylon 6.6, 30% Glass Fiber
- Hexcel® HexPly® F155 Epoxy Resin, 181 Glass Fabric
- Abatron AboCoat 8709-12/AboCure 50-12 Silver-Filled Electrically Conductive Epoxy Compound
- 3M Novec™ 8200 Engineered Fluid
Copyright © lookpolymers.com All Rights Reserved