Toyobo T-750 Nylon, Painting Grade
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Toyobo |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo T-750 Nylon, Painting Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Feature: Glass fiber and mineral reinforced, high heat distortion gradesInformation provided by Toyobo Co., Ltd
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ASTM D792 |
| Water Absorption | 0.70 % | 0.70 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm @Thickness 3.00 mm |
0.0030 in/in @Thickness 0.118 in |
|
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 3.00 mm |
0.0080 in/in @Thickness 0.118 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Ultimate | 123 MPa | 17800 psi | ASTM D638 |
| Elongation at Break | 3.8 % | 3.8 % | ASTM D638 |
| Modulus of Elasticity | 7.20 GPa | 1040 ksi | ASTM D638 |
| Flexural Yield Strength | 183 MPa | 26500 psi | ASTM D790 |
| Flexural Modulus | 7.20 GPa | 1040 ksi | ASTM D790 |
| Izod Impact, Notched | 1.20 J/cm | 2.25 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 43.0 µm/m-°C @Temperature 20.0 °C |
23.9 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C | 423 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C | 397 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | unregistered |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 22.0 kV/mm @Thickness 2.00 mm |
559 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Ovation Polymers Opnyl OP6GF15 Nylon 6, 15% Glass Reinforced, Dry
- Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 7.9 mm thick plate, aged 3 hours at 816°C
- Sylvin Technologies 8600-95 Clear PVC Extrusion Compound
- SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR2210 PC (Europe-Africa-Middle East)
- Loctite® 4061 Cyanoacrylate Adhesive
- Dow Corning XIAMETER® PMCPMEM-0346 Emulsion
- DuPont Performance Polymers Neoprene 750 Copolymer of chloroprene and 2,3,dichloro-1,3,-butadiene
- Azdel SuperLite® SL551800-100 PP Resin Matrix / 55% Glass Fiber (3 mm Molded Thickness)
- BASF Methyl Acrylate
- Addcomp ADD-VANCE® SA 420 Slip/anti-block additive
Copyright © lookpolymers.com All Rights Reserved