Network Polymers MS 150 IF Styrene Methyl Methacrylate Terpolymer
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Polystyrene (PS) , Styrene/Methyl Methacrylate Copolymer (SMMA) |
| Manufacturer | Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Network Polymers MS 150 IF Styrene Methyl Methacrylate Terpolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Styrene Methyl Methacrylate TerpolymerInformation provided by Network Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 4.1 g/10 min @Load 5.00 kg, Temperature 200 °C |
4.1 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 75 | 75 | ASTM D2240 |
| Tensile Strength at Break | 34.42 MPa | 4992 psi | chs 2 in/min; ASTM D638 |
| Elongation at Break | 31 % | 31 % | chs 2 in/min; ASTM D638 |
| Modulus of Elasticity | 2.20 GPa | 319 ksi | ASTM D638 |
| Flexural Modulus | 1.83 GPa | 266 ksi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm | 0.500 ft-lb/in | 0.125 inch bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 83.0 °C | 181 °F | Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| Vicat Softening Point | 97.0 °C | 207 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 89 % | 89 % | ASTM D1003 |
Users viewing this material also viewed the following:
- PolyOne Nymax™ GMF 600 40 Black 117 V P1 Polyamide 6 (Nylon 6)
- Plastcom SLOVAMID® 6 T 30 FRC 4 TS PA6 flame retarded, heat stabilized
- PolyOne Geon™ Vinyl Flexible A8000 Polyvinyl Chloride, Flexible (PVC, Flexible)
- SABIC Innovative Plastics Cycoloy® CP8930 PC+ABS (Asia Pacific)
- Imerys Mercapâ„¢ 100 Kaolin
- ChevronTexaco Canopus® 32
- ExxonMobil Bicor™ 21MB777 OPP Film
- ExxonMobil LLDPE LL 3404.48 Linear Low Density Polyethylene Resin
- Addcomp ADD-VANCE® CL 510 Clarification Masterbatch with Random Copolymer PP carrier
- Fiberfil® J-68/30/E/UV Polypropylene Copolymer, 30% Glass Fiber Reinforced, Chemically coupled, UV Stabilized
Copyright © lookpolymers.com All Rights Reserved