Toyobo T-422T Nylon, Mineral-Reinforced
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Toyobo |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo T-422T Nylon, Mineral-Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Feature: High heat distortion and good toughnessInformation provided by Toyobo Co., Ltd
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ASTM D792 |
| Water Absorption | 0.70 % | 0.70 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0050 cm/cm @Thickness 3.00 mm |
0.0050 in/in @Thickness 0.118 in |
|
| Linear Mold Shrinkage, Transverse | 0.0055 cm/cm @Thickness 3.00 mm |
0.0055 in/in @Thickness 0.118 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Ultimate | 91.0 MPa | 13200 psi | ASTM D638 |
| Elongation at Break | 4.7 % | 4.7 % | ASTM D638 |
| Modulus of Elasticity | 5.90 GPa | 856 ksi | ASTM D638 |
| Flexural Yield Strength | 137 MPa | 19900 psi | ASTM D790 |
| Flexural Modulus | 6.40 GPa | 928 ksi | ASTM D790 |
| Izod Impact, Notched | 1.70 J/cm | 3.18 ft-lb/in | ASTM D256 |
| Taber Abrasion, mg/1000 Cycles | 30 | 30 | CS-17 wheel; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 48.0 µm/m-°C @Temperature 20.0 °C |
26.7 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | unregistered |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 29.0 kV/mm @Thickness 2.00 mm |
737 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Arc Resistance | 123 sec | 123 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Taiwan Sheen Soon Sheenthane® AS-626H TPU for PU Adhesive
- Star Plastics PC741 Molding Grade PC
- A. Schulman POLYTROPE™ TPP 408 Blow Molding Grade Olefinic Thermoplastic Elastomer
- Total PPH 9082 Polypropylene, Homopolymer
- Chevron Phillips Marlex® 9004 HDPE Injection Molding Resin
- Diamond Polymers NPP25-0616 Black Impact Modified Polypropylene
- Polyplastics Duracon® EB-08 Acetal Co-polymer (POM), Conductive, Antistatic
Copyright © lookpolymers.com All Rights Reserved