- M. Holland Company MAGMA® LM112-K LLDPE (discontinued **)
M. Holland Company MAGMA® LM112-K LLDPE (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Rotational Molding Grade |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | M. Holland Company MAGMA® LM112-K LLDPE
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Good Heat Seal, Good Processability, Good Tear Strength, Good ToughnessProcessing Method: ExtrusionInformation provided by M. Holland.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.913 g/cc | 0.0330 lb/in³ | ASTM D1505 |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 520 % | 520 % | ASTM D882 |
| Film Elongation at Break, TD | 710 % | 710 % | ASTM D882 |
| Elmendorf Tear Strength MD | 390 g | 390 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 750 g | 750 g | ASTM D1922 |
| Dart Drop Test | 380 g | 0.838 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 36.9 MPa | 5350 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 19.3 MPa | 2800 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 104 °C | 220 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | <= 149 °C | <= 300 °F | |
| Zone 1 | 149 °C | 300 °F | |
| Melt Temperature | 182 - 232 °C | 360 - 450 °F | |
| Die Opening | 0.0810 - 0.254 cm | 0.0319 - 0.100 in | |
| Blow-up Ratio (BUR) | 1.5 - 3.0 | 1.5 - 3.0 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Pellets |
Users viewing this material also viewed the following:
- Resinlab® CYNERGY CA6812 Adhesive
- Lanxess Durethan® A 30 S H3.0 000000 Nylon 66, Injection Molding
- Huntsman AVALON® 95 AE Thermoplastic Polyurethane
- Teknor Apex APEX® 3201-50 Polyvinyl Chloride, Flexible
- A. Schulman FORMION™ FI 234 20% Mineral Reinforced Ionomer / Nylon Alloy
- DuPont Teijin Films Mylar® M34 Polyester Film, 75 Gauge (20 µm), PVDC Coated
- Fainplast Compounds GS 61 Flexible PVC, Injection Molding for Footwear
- Asia International Enterprise (Hong Kong) 60T4 Nylon 66, 20% Filled
- Arlon 55276R026 0.026" (0.660 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- SABIC Innovative Plastics NORYL GTX GTX6203 PPE+PA (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved