- Toyobo NB-5620S Nylon/Olefin Alloy, 15% Mineral Reinforced (Conditioned)
Toyobo NB-5620S Nylon/Olefin Alloy, 15% Mineral Reinforced (Conditioned)
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Toyobo |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo NB-5620S Nylon/Olefin Alloy, 15% Mineral Reinforced (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: 15% Mineral Reinforced, Light WeightInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | (DAM); ASTM D792 |
| Filler Content | 15 % | 15 % | |
| Water Absorption | 0.50 % | 0.50 % | 24 hrs at 23°C (DAM); ASTM D570 |
| 2.1 % | 2.1 % | 65% R.H. equilibrium (DAM); ASTM D570 | |
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm @Thickness 1.00 mm |
0.0060 - 0.0080 in/in @Thickness 0.0394 in |
DAM |
| 0.014 - 0.018 cm/cm @Thickness 3.00 mm |
0.014 - 0.018 in/in @Thickness 0.118 in |
DAM |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 52.0 MPa | 7540 psi | ASTM D638 |
| 90.0 MPa @Temperature -40.0 °C |
13100 psi @Temperature -40.0 °F |
ASTM D638 | |
| Tensile Strength, Ultimate | 22.0 MPa @Temperature 80.0 °C |
3190 psi @Temperature 176 °F |
ASTM D638 |
| Flexural Strength | 79.0 MPa | 11500 psi | ASTM D790 |
| 30.0 MPa @Temperature 80.0 °C |
4350 psi @Temperature 176 °F |
ASTM D790 | |
| 152 MPa @Temperature -40.0 °C |
22000 psi @Temperature -40.0 °F |
ASTM D790 | |
| Flexural Modulus | 2.30 GPa | 334 ksi | ASTM D790 |
| 1.40 GPa @Temperature 80.0 °C |
203 ksi @Temperature 176 °F |
ASTM D790 | |
| 5.40 GPa @Temperature -40.0 °C |
783 ksi @Temperature -40.0 °F |
ASTM D790 | |
| Izod Impact, Notched | 0.600 J/cm @Temperature -40.0 °C |
1.12 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| 2.20 J/cm @Temperature 23.0 °C |
4.12 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 |
| Dielectric Strength | 21.0 kV/mm @Thickness 2.00 mm |
533 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 290 °C | 464 - 554 °F | (DAM) |
| Mold Temperature | 50.0 - 120 °C | 122 - 248 °F | (DAM) |
| Injection Pressure | 50.0 MPa | 7250 psi | (DAM) |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE D 4701 GREY
- SABIC Innovative Plastics LNP COLORCOMP DX04401H PC
- Materion Beryllium Copper Alloy 165 Plate & Rolled Bar; H (TD04) Temper; over 9.5 to 25 mm Thickness (UNS C17000)
- MetalTek MTEK Super 20-32Nb Cast UNS N08151 Heat Resistant Stainless Steel
- Teknor Apex Synres® PP HFR005 Polypropylene
- Chevron Phillips MarFlex® 9607 HDPE Cast Film Resin
- ExxonMobil Hicor® 30 HT 103 OHD Film
- DuPont Teijin Films Teijin® Tetoron® U4 Polyester Film, 300 Gauge
- Arlon 56810R025 0.025" (0.635 mm) Uncured Silicone Rubber with Fiberglass Substrate
- ATI Allvac® Nickelvac® C 22 UNS N06022 Nickel Superalloy
Copyright © lookpolymers.com All Rights Reserved