Toyobo GLAMIDE® TY-502NZ 6T-Nylon
| Category | Polymer , Thermoplastic , Nylon , Nylon, Aromatic |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo GLAMIDE® TY-502NZ 6T-Nylon.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade TY-502NZ is a non-reinforced, aromatic 6T-Nylon with a high melting point.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | Absolute Drying; ASTM-D792 |
| Water Absorption | 0.70 % | 0.70 % | Absolute Drying; ASTM-D570 |
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm @Thickness 1.00 mm |
0.0020 - 0.0040 in/in @Thickness 0.0394 in |
Absolute Drying |
| 0.0050 - 0.0080 cm/cm @Thickness 3.00 mm |
0.0050 - 0.0080 in/in @Thickness 0.118 in |
Absolute Drying | |
| Melt Flow | 7.0 g/10 min | 7.0 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 28.0 MPa @Temperature 80.0 °C |
4060 psi @Temperature 176 °F |
Practical Use (Water Absorption 1.9%); ASTM-D638 |
| 50.0 MPa @Temperature 80.0 °C |
7250 psi @Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 85.0 MPa @Temperature 23.0 °C |
12300 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 1.9%); ASTM-D638 | |
| 90.0 MPa @Temperature 23.0 °C |
13100 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 106 MPa @Temperature -40.0 °C |
15400 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 1.9%); ASTM-D638 | |
| 110 MPa @Temperature -40.0 °C |
16000 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | 20 % | 20 % | ASTM-D638 |
| Flexural Strength | 45.0 MPa @Temperature 80.0 °C |
6530 psi @Temperature 176 °F |
Practical Use (Water Absorption 1.9%); ASTM-D790 |
| 80.0 MPa @Temperature 80.0 °C |
11600 psi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 130 MPa @Temperature 23.0 °C |
18900 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 1.9%); ASTM-D790 | |
| 145 MPa @Temperature 23.0 °C |
21000 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 155 MPa @Temperature -40.0 °C |
22500 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 1.9%); ASTM-D790 | |
| 160 MPa @Temperature -40.0 °C |
23200 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 1.00 GPa @Temperature 80.0 °C |
145 ksi @Temperature 176 °F |
Practical Use (Water Absorption 1.9%); ASTM-D790 |
| 2.50 GPa @Temperature 80.0 °C |
363 ksi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 3.40 GPa @Temperature 23.0 °C |
493 ksi @Temperature 73.4 °F |
Practical Use (Water Absorption 1.9%); ASTM-D790 | |
| 3.50 GPa @Temperature 23.0 °C |
508 ksi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 4.20 GPa @Temperature -40.0 °C |
609 ksi @Temperature -40.0 °F |
Practical Use (Water Absorption 1.9%); ASTM-D790 | |
| 4.50 GPa @Temperature -40.0 °C |
653 ksi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Compressive Strength | 100 MPa | 14500 psi | Absolute Drying; ASTM-D695 |
| Izod Impact, Notched | 0.600 J/cm @Temperature 23.0 °C |
1.12 ft-lb/in @Temperature 73.4 °F |
Practical Use (Water Absorption 1.9%); ASTM-D256 |
| 0.700 J/cm @Temperature -40.0 °C |
1.31 ft-lb/in @Temperature -40.0 °F |
Practical Use (Water Absorption 1.9%); ASTM-D256 | |
| 0.700 J/cm @Temperature -40.0 °C |
1.31 ft-lb/in @Temperature -40.0 °F |
Absolute Drying; ASTM-D256 | |
| 1.20 J/cm @Temperature 23.0 °C |
2.25 ft-lb/in @Temperature 73.4 °F |
Absolute Drying; ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 55.0 µm/m-°C | 30.6 µin/in-°F | Absolute Drying; ASTM-D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | Absolute Drying; ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM-D257 |
| Dielectric Constant | 4.0 @Frequency 1000 Hz |
4.0 @Frequency 1000 Hz |
ASTM-D150 |
| Dielectric Strength | 22.0 kV/mm @Thickness 2.00 mm |
559 kV/in @Thickness 0.0787 in |
Practical Use (Water Absorption 1.9%); ASTM-D149 |
| 23.0 kV/mm @Thickness 2.00 mm |
584 kV/in @Thickness 0.0787 in |
Absolute Drying; ASTM-D149 | |
| Arc Resistance | 130 sec | 130 sec | ASTM-D495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 305 - 320 °C | 581 - 608 °F | |
| Mold Temperature | 90.0 °C | 194 °F | |
| Injection Pressure | 30.0 - 40.0 MPa | 4350 - 5800 psi |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 3101-10 Fiberglass Reinforced Thermoset BMC
- Stir SpA T 3099 A (PVC)
- Polyram RamTal PM1509 Acetal, Low Friction
- A. Schulman FORMION™ FI 120 Non-Reinforced, Injection Molding Grade Zinc Ionomer
- Ascend Performance Materials Vydyne® R550H Nylon 66, 50% Glass Reinforced, Conditioned
- ConocoPhillips ANDEROL® FGH 46 Synthetic Food Grade Hydraulic Fluid, ISO 46
- Asahi Kasei Delpet® 80N Acrylic Molding Compound, High Heat Grade
- Beijing Ranger Chem SM-604R Solid Epoxy Resin
Copyright © lookpolymers.com All Rights Reserved