Clariant Renol PPOSP0001 Polyphenylene Oxide, Mineral Filled
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Mineral Filled |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol PPOSP0001 Polyphenylene Oxide, Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.62 g/cc | 1.62 g/cc | ASTM D792 |
| Filler Content | 50 % | 50 % | ASTM D2584 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.3 MPa | 7300 psi | ASTM D638 |
| Elongation at Break | 2.0 - 3.0 % | 2.0 - 3.0 % | ASTM D638 |
| Flexural Yield Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 11.7 GPa | 1700 ksi | ASTM D790 |
| Izod Impact, Notched | 0.160 J/cm @Temperature 22.8 °C |
0.300 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 107 °C | 225 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.17 mm |
V-0 @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 288 °C | 500 - 550 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Dry Time | 3 - 4 hour @Temperature 93.3 °C |
3 - 4 hour @Temperature 200 °F |
|
| Injection Pressure | 41.4 - 74.5 MPa | 6000 - 10800 psi | Secondary |
| 68.9 - 124 MPa | 10000 - 18000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- SABIC M40053S High Density Polyethylene for Injection Molding
- Precision Polymer Engineering E70A Ethylene Propylene Rubber
- Radici Heraflex® P 40D 11 I HF 1530 Modified Polypropylene
- Gouda Vuurvast GOLITE 1.0.6. Mix Refractory Insulating Castable
- Techmer ES Elastoblend® PA6 GF30 IM L 30% Glass Filled
- Borealis RA130E-1498 Polypropylene Random Copolymer
- Plenco 6500 Phenolic, Briquette, Injection Molded
- Dow Corning 1248 Fluid
- ConocoPhillips Hydroclear® 68 Turbine Oil
Copyright © lookpolymers.com All Rights Reserved