Toyobo GLAMIDE® T-714E Transparent Nylon
| Category | Polymer , Thermoplastic , Nylon , Nylon, Aromatic |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo GLAMIDE® T-714E Transparent Nylon.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade T-714E is a non-reinforced, non-spherulite, aromatic, and transparent nylon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | Absolute Drying; ASTM-D792 |
| Water Absorption | 1.3 % | 1.3 % | Absolute Drying; ASTM-D570 |
| Moisture Absorption at Equilibrium | 2.4 % | 2.4 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm @Thickness 1.00 mm |
0.0010 - 0.0030 in/in @Thickness 0.0394 in |
Absolute Drying |
| 0.0040 - 0.0070 cm/cm @Thickness 3.00 mm |
0.0040 - 0.0070 in/in @Thickness 0.118 in |
Absolute Drying |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 16.0 MPa @Temperature 80.0 °C |
2320 psi @Temperature 176 °F |
Practical Use (Water Absorption 2.4%); ASTM-D638 |
| 80.0 MPa @Temperature 80.0 °C |
11600 psi @Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 92.0 MPa @Temperature 23.0 °C |
13300 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.4%); ASTM-D638 | |
| 97.0 MPa @Temperature 23.0 °C |
14100 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 125 MPa @Temperature -40.0 °C |
18100 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.4%); ASTM-D638 | |
| 130 MPa @Temperature -40.0 °C |
18900 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | 50 % | 50 % | ASTM-D638 |
| Flexural Strength | 25.0 MPa @Temperature 80.0 °C |
3630 psi @Temperature 176 °F |
Practical Use (Water Absorption 2.4%); ASTM-D790 |
| 121 MPa @Temperature 80.0 °C |
17500 psi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 135 MPa @Temperature 23.0 °C |
19600 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.4%); ASTM-D790 | |
| 147 MPa @Temperature 23.0 °C |
21300 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 185 MPa @Temperature -40.0 °C |
26800 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.4%); ASTM-D790 | |
| 195 MPa @Temperature -40.0 °C |
28300 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 0.500 GPa @Temperature 80.0 °C |
72.5 ksi @Temperature 176 °F |
Practical Use (Water Absorption 2.4%); ASTM-D790 |
| 2.00 GPa @Temperature 80.0 °C |
290 ksi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 2.50 GPa @Temperature 23.0 °C |
363 ksi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.4%); ASTM-D790 | |
| 2.60 GPa @Temperature 23.0 °C |
377 ksi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 3.50 GPa @Temperature -40.0 °C |
508 ksi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.4%); ASTM-D790 | |
| 3.80 GPa @Temperature -40.0 °C |
551 ksi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Compressive Strength | 100 MPa | 14500 psi | Absolute Drying; ASTM-D695 |
| Izod Impact, Notched | 0.200 J/cm @Temperature -40.0 °C |
0.375 ft-lb/in @Temperature -40.0 °F |
ASTM-D256 |
| 0.600 J/cm @Temperature 23.0 °C |
1.12 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 54.0 µm/m-°C | 30.0 µin/in-°F | Absolute Drying; ASTM-D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | Absolute Drying; ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | HB | HB |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM-D257 |
| Dielectric Constant | 4.0 @Frequency 1000 Hz |
4.0 @Frequency 1000 Hz |
ASTM-D150 |
| Dielectric Strength | 19.0 kV/mm @Thickness 2.00 mm |
483 kV/in @Thickness 0.0787 in |
ASTM-D149 |
| Arc Resistance | 110 sec | 110 sec | ASTM-D495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 280 °C | 482 - 536 °F | |
| Mold Temperature | 60.0 °C | 140 °F | |
| Injection Pressure | 40.0 - 50.0 MPa | 5800 - 7250 psi |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufFill™ 5000-SN4 PP, Flame Retardant
- LATI Latilub 75/4-15ST G/30 PBT, 30% Glass Fiber Reinforced, Silicone/PTFE Filled
- Schmolz + Bickenbach MoldMAX® SC Copper Alloy
- Westlake Epolene® C-13P Coating Grade - Branched Medium Molecular Weight Polyethylene Polymer
- Zyvex Performance Materials Aroply™ 350 Nano-Engineered Composite Film Adhesive
- Eastman Tenite Propionate 383A2R30007 Natural, Trsp Cellulose Acetate Propionate
- Covestro Makrolon® 2658 Polycarbonate, Injection Grade
- Bohler-Uddeholm UDDEHOLM VANADIS 6 Cold Work Tool Steel
- A. Schulman ComAlloy Hiloy® 624 Nylon 6/6, Glass Reinforced
- Techmer ES Plastiblend® ABS/PBT GF15
Copyright © lookpolymers.com All Rights Reserved