Total PPH 6080 Polypropylene Homopolymer, Cast Film

Category Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Total Atofina
Trade Name PPH
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total PPH 6080 Polypropylene Homopolymer, Cast Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polypropylene PPH 6080 is a homopolymer polypropylene with a Melt Flow index of 9 g/10 min for the cast extrusion of film with excellent optical properties and good sterilizability.Polypropylene PPH 6080 can be used as single layer films as well as the core layer of coextruded films, for food packaging, hosiery packaging, shirt packaging, lamination films, ... as well as for stationary supplies.Information provided by Total Petrochemicals.
Physical Properties Metric English Comments
Specific Gravity 0.905 g/cc
0.905 g/cc
ISO 1183
Bulk Density 0.525 g/cc
0.0190 lb/in³
ISO 1183
Thickness 50.0 microns
1.97 mil
Melt Flow 9.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
9.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 95
95
ISO 2039-2
Film Tensile Strength at Yield, MD 23.0 MPa
3340 psi
ISO 527-3
Film Tensile Strength at Yield, TD 23.0 MPa
3340 psi
ISO 527-3
Tensile Strength, Yield 30.0 MPa
4350 psi
ISO 527-2
Film Elongation at Break, MD 650 %
650 %
ISO 527-3
Film Elongation at Break, TD 600 %
600 %
ISO 527-3
Elongation at Yield 10 %
10 %
ISO 527-2
Tensile Modulus 1.45 GPa
210 ksi
ISO 527-2
Flexural Modulus 1.35 GPa
196 ksi
ISO 178
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
ISO 180
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
ISO 179
Elmendorf Tear Strength, MD 1.70 g/micron
43.2 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 2.00 g/micron
50.8 g/mil
ISO 6383-2
Dart Drop Test 270 g
0.595 lb
ISO 7765-1
Film Tensile Strength at Break, MD 51.0 MPa
7400 psi
ISO 527-3
Film Tensile Strength at Break, TD 42.0 MPa
6090 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 160 °C
320 °F
ISO 3146
Deflection Temperature at 0.46 MPa (66 psi) 100 °C
212 °F
120°C per hour; ISO 752
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
120°C per hour; ISO 752
Vicat Softening Point 87.0 °C

@Load 5.10 kg
189 °F

@Load 11.2 lb
50°C per hour; ISO 306
152 °C

@Load 1.02 kg
306 °F

@Load 2.25 lb
50°C per hour; ISO 306
Optical Properties Metric English Comments
Haze 0.10 %
0.10 %
ISO 14782
Gloss 91 %
91 %
at 45°; ASTM D2457