- Teknor Apex Monprene® MP-2290 Thermoplastic Elastomer
Teknor Apex Monprene® MP-2290 Thermoplastic Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Teknor Apex Company |
| Trade Name | MONPRENE® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teknor Apex Monprene® MP-2290 Thermoplastic Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Forms: Pellets Processing Method: Extrusion; Injection Molding Injection Notes: Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C); Injection Rate: Fast Extrusion Notes: Screw Speed: 30 to 100 rpmInformation Provided by Teknor Apex
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.890 g/cc | 0.890 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.030 cm/cm | 0.030 in/in | ASTM D955 |
| Melt Flow | 1.50 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.50 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 45 | 45 | ASTM D2240 |
| Tensile Strength at Break | 4.14 MPa | 600 psi | ASTM D412 |
| Tensile Stress | 3.45 MPa @Strain 300 % |
500 psi @Strain 300 % |
ASTM D412 |
| Elongation at Break | 480 % | 480 % | ASTM D412 |
| Compression Set | 20 % @Temperature 22.8 °C, Time 79200 sec |
20 % @Temperature 73.0 °F, Time 22.0 hour |
ASTM D395B |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 65.0 °C | 149 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 182 - 232 °C | 360 - 450 °F | |
| Middle Barrel Temperature | 188 - 238 °C | 370 - 460 °F | |
| Front Barrel Temperature | 193 - 243 °C | 380 - 470 °F | |
| Nozzle Temperature | 199 - 249 °C | 390 - 480 °F | |
| Zone 1 | 182 - 232 °C | 360 - 450 °F | |
| Zone 2 | 188 - 238 °C | 370 - 460 °F | |
| Zone 3 | 193 - 243 °C | 380 - 470 °F | |
| Zone 5 | 199 - 249 °C | 390 - 480 °F | |
| Die Temperature | 199 - 249 °C | 390 - 480 °F | |
| Melt Temperature | 199 - 249 °C | 390 - 480 °F | Processing Temperature |
| Mold Temperature | 35.0 - 48.9 °C | 95.0 - 120 °F | |
| Injection Pressure | 1.38 - 5.52 MPa | 200 - 800 psi | |
| Back Pressure | 0.172 - 0.689 MPa | 25.0 - 100 psi | |
| Cushion | 0.381 - 2.54 cm | 0.150 - 1.00 in | |
| Screw Speed | 50 - 100 rpm | 50 - 100 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Clear/Transparent |
Users viewing this material also viewed the following:
- Precision Polymer Engineering Q70Y Polyurethane Rubber
- Premix Premi-Glas® 2550® CR-SX Fiberglass Reinforced Thermoset SMC
- Humiseal 1A33LSE Urethane Conformal Coating
- LG Chemical B120 EPS, Non-Flame Retardant
- Gromax Standard GB9567-97
- Hexcel® HexPly® F593 Epoxy Resin, W3T282 Carbon Fabric
- Lubrizol Estane® GP 58 DT Thermoplastic Polyurethane
- California Fine Wire NIFE 5200 Nickel Iron Resistance Wire
- 3M Scotch-Weld™ TL72 Threadlocker Anaerobic Adhesive
Copyright © lookpolymers.com All Rights Reserved