Total PPC 10641 Polypropylene, Heterophasic Copolymer, Injection Molding

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded
Manufacturer Total Atofina
Trade Name PPC
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total PPC 10641 Polypropylene, Heterophasic Copolymer, Injection Molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polypropylene PPC 10641 is a nucleated antistatic heterophasic copolymer with high Melt Flow index of 44 g/10 min.Polypropylene PPC 10641 is characterized by high fluidity with good mechanical properties.Polypropylene PPC 10641 has been specially developed for high speed injection molding of food packaging.Peroxide is not used in the manufacturing of this product.Information provided by Total Petrochemicals.
Physical Properties Metric English Comments
Specific Gravity 0.905 g/cc
0.905 g/cc
ISO 1183
Bulk Density 0.525 g/cc
0.0190 lb/in³
ISO 1183
Melt Flow 44 g/10 min

@Load 2.16 kg,
Temperature 230 °C
44 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 100
100
ISO 2039-2
Tensile Strength, Yield 27.0 MPa
3920 psi
ISO 527-2
Elongation at Yield 4.0 %
4.0 %
ISO 527-2
Tensile Modulus 1.60 GPa
232 ksi
ISO 527-2
Flexural Modulus 1.50 GPa
218 ksi
ISO 178
Izod Impact, Notched (ISO) 4.00 kJ/m²

@Temperature -20.0 °C
1.90 ft-lb/in²

@Temperature -4.00 °F
ISO 180
7.50 kJ/m²

@Temperature 23.0 °C
3.57 ft-lb/in²

@Temperature 73.4 °F
ISO 180
Charpy Impact, Notched 0.450 J/cm²

@Temperature -20.0 °C
2.14 ft-lb/in²

@Temperature -4.00 °F
ISO 179
0.700 J/cm²

@Temperature 23.0 °C
3.33 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
Melting Point 165 °C
329 °F
ISO 3146
Deflection Temperature at 0.46 MPa (66 psi) 114 °C
237 °F
120°C per hour; ISO 752
Deflection Temperature at 1.8 MPa (264 psi) 57.0 °C
135 °F
120°C per hour; ISO 752
Vicat Softening Point 80.0 °C

@Load 5.10 kg
176 °F

@Load 11.2 lb
50°C per hour; ISO 306
148 °C

@Load 1.02 kg
298 °F

@Load 2.25 lb
50°C per hour; ISO 306