Teijin PanliteÂ® AD-5503 Optical Use Polycarbonate Resin

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded
Manufacturer	Teijin
Trade Name	Panlite®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Teijin PanliteÂ® AD-5503 Optical Use Polycarbonate Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

High fluidity grade for optical media that provides low optical distortion moldings. Impurities in pellets are severely controlled, and resulting high quality is obtaining good reputation.Applications:Optical disc moldings such as CD, CD-ROM, MO, MD and DVD.Optical lens moldings.Information provided by Teijin Chemicals Ltd.

Physical Properties	Metric	English	Comments
Density	1.20 g/cc	0.0434 lb/inÂ³	ISO 1183
Water Absorption	0.20 %	0.20 %	in water, 23Â°C, 24h; ISO 62
Linear Mold Shrinkage	0.0050 - 0.0070 cm/cm @Thickness 4.00 mm	0.0050 - 0.0070 in/in @Thickness 0.157 in
Linear Mold Shrinkage, Transverse	0.0050 - 0.0070 cm/cm @Thickness 4.00 mm	0.0050 - 0.0070 in/in @Thickness 0.157 in
Melt Flow	64.8 g/10 min @Load 1.20 kg, Temperature 300 Â°C	64.8 g/10 min @Load 2.65 lb, Temperature 572 Â°F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	63.0 MPa	9140 psi	50mm/min; ISO 527
Elongation at Break	>= 50 %	>= 50 %	50mm/min; ISO 527
Elongation at Yield	6.0 %	6.0 %	50mm/min; ISO 527
Tensile Modulus	2.45 GPa	355 ksi	1mm/min; ISO 527
Flexural Strength	96.0 MPa	13900 psi	2mm/min; ISO 178
Flexural Modulus	2.40 GPa	348 ksi	2mm/min; ISO 178
Charpy Impact Unnotched	NB	NB	ISO 179
Charpy Impact, Notched	3.00 J/cmÂ²	14.3 ft-lb/inÂ²	ISO 179

Thermal Properties	Metric	English	Comments
CTE, linear	70.0 Âµm/m-Â°C @Temperature 20.0 Â°C	38.9 Âµin/in-Â°F @Temperature 68.0 Â°F	ISO 11359
CTE, linear, Transverse to Flow	70.0 Âµm/m-Â°C @Temperature 20.0 Â°C	38.9 Âµin/in-Â°F @Temperature 68.0 Â°F	ISO 11359
Deflection Temperature at 0.46 MPa (66 psi)	138 Â°C	280 Â°F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	124 Â°C	255 Â°F	ISO 75
Vicat Softening Point	143 Â°C	289 Â°F	50Â°C/hr, 50N; ISO 306

Optical Properties	Metric	English	Comments
Refractive Index	1.585	1.585	ASTM D542
Transmission, Visible	89 % @Thickness 3.00 mm	89 % @Thickness 0.118 in	ASTM D1003

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm	IEC 60093
Dielectric Constant	3.0 @Frequency 1e+6 Hz	3.0 @Frequency 1e+6 Hz	IEC 60250
	3.1 @Frequency 100 Hz	3.1 @Frequency 100 Hz	IEC 60250
Dielectric Strength	30.0 kV/mm	762 kV/in	IEC 60243
Dissipation Factor	0.0010 @Frequency 100 Hz	0.0010 @Frequency 100 Hz	IEC 60250
	0.0090 @Frequency 1e+6 Hz	0.0090 @Frequency 1e+6 Hz	IEC 60250
Comparative Tracking Index	250 V	250 V	IEC 60112