Teijin Multilon DN-1530B Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate (PC) |
| Manufacturer | Teijin |
| Trade Name | Multilon |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teijin Multilon DN-1530B Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. It has improved stiffness through the addition of 30 % filler. Improved stiffness and high fluidity realizes a thin wall of OA machines etc.Applications:Thin wall components of mechanical, electric and electronic equipment that need least warpage and dimensional accuracy etc.Information provided by Teijin Chemicals Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm @Thickness 4.00 mm |
0.0010 - 0.0030 in/in @Thickness 0.157 in |
|
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0040 cm/cm @Thickness 4.00 mm |
0.0020 - 0.0040 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | 50mm/min; ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | 50mm/min; ISO 527 |
| Tensile Modulus | 9.00 GPa | 1310 ksi | 1mm/min; ISO 527 |
| Flexural Strength | 110 MPa | 16000 psi | 2mm/min; ISO 178 |
| Flexural Modulus | 8.00 GPa | 1160 ksi | 2mm/min; ISO 178 |
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C @Temperature 20.0 °C |
16.7 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| CTE, linear, Transverse to Flow | 35.0 µm/m-°C @Temperature 20.0 °C |
19.4 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | ISO 75 |
| Vicat Softening Point | 122 °C | 252 °F | 50°C/hr, 50N; ISO 306 |
| Flammability, UL94 | V-1 @Thickness 1.50 mm |
V-1 @Thickness 0.0591 in |
black |
| V-1 @Thickness 3.00 mm |
V-1 @Thickness 0.118 in |
||
| 5VB @Thickness 2.00 mm |
5VB @Thickness 0.0787 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 60093 |
Users viewing this material also viewed the following:
- ICO Polymers ICORENEâ„¢ 110-1332 LMDPE Rotational Molding Resin
- Solvay Specialty Polymers Catalyst CT/1 Polyolefin
- A. Schulman POLYFORT™ FPP 1245 CaCO3 Filled Copolymer Polypropylene
- Toyobo VYLOPET® EMC132-01 Injection Molding Polyester Resin, Flame Resistant
- ChevronTexaco TC-W3 2-Cycle Oil
- DuPont Teijin Films Mylar® RL33 Polyester Packaging Film, 100 Gauge
- Addiplast Addilene J 430 N30 Polypropylene Copolymer
- Lanxess Pocan® B 3235 XF 000000 PBT, 30% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved