Carpenter Micro-Melt® 9 Tough Treated Tool Steel

Category	Metal , Ferrous Metal , Tool Steel
Manufacturer	Carpenter Technology Corporation (Cartech)
Trade Name	Micro-Melt®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Carpenter Micro-Melt® 9 Tough Treated Tool Steel.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Micro-Melt® 9 tool steel is a high vanadium tool steel produced using the Carpenter Micro-Melt powder process. This grade possesses wear resistance superior to most other tool steels along with good strength and toughness characteristics. In addition, it provides higher toughness characteristics than Micro-Melt® 10 alloy with slightly lower wear resistance. Micro-Melt 9 tool steel changes size only slightly after hardening. An expansion of about 0.0005 inches/inch is typical.Applications: punches, dies for blanking, piercing dies, forming rolls and dies, cold heading, steel mill rolls, cold extrusion, slitter knives, shears, pelletizer blades, nozzles, woodworking tools, cold extrusion barrels, cold extrusion liners, plastic injection molds, compacting toolsInformation provided by Carpenter Technology Corporation.Micro-Melt® is a registered trademark of Carpenter Technology Corporation.

Physical Properties	Metric	English	Comments
Specific Gravity	7.45 g/cc	7.45 g/cc

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell C	49	49
Tensile Strength at Break	4171 MPa	605000 psi
Tensile Strength, Ultimate	4206 MPa	610000 psi
Modulus of Elasticity	200 GPa	29000 ksi
Izod Impact Unnotched	40.67 J	30.00 ft-lb	Transverse
	135.6 J	100.0 ft-lb	Longitudinal
Abrasion	16.3	16.3	loss in mm<sup>3</sup>, after 30 minutes; ASTM G65

Component Elements Properties	Metric	English	Comments
Carbon, C	1.7 - 1.85 %	1.7 - 1.85 %
Chromium, Cr	4.75 - 5.75 %	4.75 - 5.75 %
Iron, Fe	79.67 - 79.7 %	79.67 - 79.7 %	As Balance
Manganese, Mn	0.35 - 0.60 %	0.35 - 0.60 %
Molybdenum, Mo	1.1 - 1.5 %	1.1 - 1.5 %
Silicon, Si	0.75 - 1.1 %	0.75 - 1.1 %
Sulfur, S	<= 0.030 %	<= 0.030 %
Vanadium, V	8.25 - 9.5 %	8.25 - 9.5 %