Zircar Ceramics ZAL-15 Alumina Insulation
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Zircar Ceramics |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Zircar Ceramics ZAL-15 Alumina Insulation.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ZAL-15 is a low thermal conductivity uniformly bound fiber board. It is ideal for machining into precision thermal insulators.Information provided by Zircar Ceramics.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.240 g/cc | 0.00867 lb/in³ | |
| Open Porosity | 93 % | 93 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 1.55 MPa @Strain 40.0 % |
225 psi @Strain 40.0 % |
Load applied normal to fiber plane, strain = load deformation in mils; Three Point Bending, Sample 0.5"*0.5"*4" |
| 1.55 MPa @Strain 25.0 % |
225 psi @Strain 25.0 % |
Load applied parallel to fiber plane, strain = load deformation in mils; Three Point Bending, Sample 0.5"*0.5"*4" | |
| Compressive Yield Strength | 0.207 MPa @Strain 2.00 % |
30.0 psi @Strain 2.00 % |
Load applied normal to fiber plane |
| 0.207 MPa @Strain 6.00 % |
30.0 psi @Strain 6.00 % |
Load applied normal to fiber plane | |
| 0.345 MPa @Strain 2.00 % |
50.0 psi @Strain 2.00 % |
Load applied parallel to fiber plane | |
| 1.24 MPa @Strain 6.00 % |
180 psi @Strain 6.00 % |
Load applied parallel to fiber plane |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 5.00 µm/m-°C @Temperature 20.0 - 1000 °C |
2.78 µin/in-°F @Temperature 68.0 - 1830 °F |
|
| Specific Heat Capacity | 1.05 J/g-°C | 0.250 BTU/lb-°F | |
| Thermal Conductivity | 0.0600 W/m-K @Temperature 250 °C |
0.416 BTU-in/hr-ft²-°F @Temperature 482 °F |
parallel to thickness; ASTM C177-76 |
| 0.0800 W/m-K @Temperature 525 °C |
0.555 BTU-in/hr-ft²-°F @Temperature 977 °F |
Parallel to Thickness; ASTM C177-76 | |
| 0.120 W/m-K @Temperature 800 °C |
0.833 BTU-in/hr-ft²-°F @Temperature 1470 °F |
Parallel to Thickness; ASTM C177-76 | |
| 0.160 W/m-K @Temperature 1075 °C |
1.11 BTU-in/hr-ft²-°F @Temperature 1967 °F |
Parallel to Thickness; ASTM C177-76 | |
| 0.220 W/m-K @Temperature 1350 °C |
1.53 BTU-in/hr-ft²-°F @Temperature 2460 °F |
Parallel to Thickness; ASTM C177-76 | |
| 0.250 W/m-K @Temperature 1350 °C |
1.74 BTU-in/hr-ft²-°F @Temperature 2460 °F |
Parallel to Thickness; ASTM C177-76 | |
| Melting Point | 1870 °C | 3400 °F | |
| Maximum Service Temperature, Air | 1550 °C | 2820 °F | Continuous |
| 1650 °C | 3000 °F | Intermittent | |
| Shrinkage | 1.00 % @Temperature 1550 °C, Time 3600 sec |
1.00 % @Temperature 2820 °F, Time 1.00 hour |
Perpendicular to Thickness |
| 3.00 % @Temperature 1650 °C, Time 3600 sec |
3.00 % @Temperature 3000 °F, Time 1.00 hour |
Perpendicular to Thickness |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 85 % | 85 % | |
| SiO2 | 15 % | 15 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | White |
Users viewing this material also viewed the following:
- Osprey Metals Ni40Cu Binary Alloy Powder (Grade 90% - 22)
- SABIC Innovative Plastics ULTEM 1000RV PEI (Asia Pacific)
- Techmer ES HiFill® PA6 GF30 HS BK 30% Glass Filled
- Universal Wire Works ER309L Stainless Steel Bare Wire
- Arkema Group ORGASOL® 1002 ES 4 Nat 1 Polyamide 6
- Abatron AboCast 7802-1/AboCure 7804-3 (80 pbw) Epoxy
- 3M 2A87 Co-Extruded Multi-Polymer Protect Tapes
- AK Steel ASTM A 907, Grade 36 Hot Rolled Carbon Steel, Structural Quality (SQ)
- Overview of materials for Polyimide, Graphite Filled
- Master Bond UV15X-6NONMED-2 Abrasion Resistant UV Curable Compound
Copyright © lookpolymers.com All Rights Reserved