Techmer ES Plastiblend® PC/PBT IM 5230
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Techmer ES |
| Trade Name | Plastiblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Plastiblend® PC/PBT IM 5230.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAdditive: Impact Modifier Features: Impact ModifiedInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Water Absorption | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm @Thickness 3.17 mm |
0.0080 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 53.8 MPa | 7800 psi | ASTM D638 |
| Elongation at Break | 110 % | 110 % | ASTM D638 |
| Flexural Yield Strength | 85.5 MPa | 12400 psi | ASTM D790 |
| Flexural Modulus | 2.10 GPa | 305 ksi | ASTM D790 |
| Izod Impact, Notched | 6.41 J/cm @Thickness 3.17 mm |
12.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 23.4 µm/m-°C | 13.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 116 °C | 240 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.1 °C | 205 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
Users viewing this material also viewed the following:
- MV Labs BI600 BiI3 Bismuth iodide
- Polymax® Maxelast® C4945E TPE, Transparent
- Global GPEI-210 10% Glass Filled Reinforced, Polyetherimide
- Momentive Performance Materials TSE392 Translucent Adhesive Sealant, Thixotropic Paste
- Wanhua Chemical Wanthane® WHT-A885 Aliphatic TPU
- Chevron Phillips MarFlex® 9659 HDPE Blown Film Resin
- Bulk Molding Compounds BMC 5436 Mineral Filled, Glass Reinforced Polyester
- Resinlab® EP1046FG Clear Electronic Grade Epoxy Encapsulant
Copyright © lookpolymers.com All Rights Reserved