Chevron Phillips Marlex® C514 HDPE Pipe and Corrugated Extrusion Resin (discontinued **)
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Extruded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chevron Phillips Marlex® C514 HDPE Pipe and Corrugated Extrusion Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics: Good melt strengthGood pipe stiffnessGood ESCRApplications: CulvertsStorm sewersLand drainageInformation provided by Chevron Phillips.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.953 g/cc | 0.0344 lb/in³ | ASTM D1505 |
| ESCR 100% Igepal® | >= 500 hour | >= 500 hour | Condition B; ASTM D1693 |
| Melt Flow | 21 g/10 min | 21 g/10 min | Condition 190/21.6, HLMI; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | 2 in/min, Type IV bar; ASTM D638 |
| Elongation at Break | >= 600 % | >= 600 % | 2 in/min, Type IV bar; ASTM D638 |
| Flexural Modulus | 1.31 GPa | 190 ksi | Tangent, 16:1 span:depth,0.5in/min; ASTM D790 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Notched Constant Ligament Stress | Min 24 h | Average of five |
Users viewing this material also viewed the following:
- PolyOne Geon™ 170 Series 179 Polyvinyl Chloride Homopolymer (PVC Homopolymer)
- Lehmann & Voss LUVOCOM® 1850-7942 PBT, with PTFE, lubricant modified
- Industrial Laminates/Norplex ES-2 Engraving Stock
- Spartech Sungard Ultra Weatherable Polycarbonate Sign Grade Sheet
- Shin-Etsu Silicones KF-6043 Fluid
- A. Schulman FORMION™ FI 120 Non-Reinforced, Injection Molding Grade Zinc Ionomer
- A. Schulman POLYTROPE™ TPP 1010E-01 Olefinic Elastomer For Sheet Extrusion
- Chevron Phillips K-Resin® DK11 Styrene-Butadiene Copolymer, Film Grade
- BASF Ultramid® B35EG3 15% Glass Filled PA6 (Conditioned)
- DuPont™ Sclairfilm® SL-1 LLDPE Film, Laminating, 76.2 µm Thickness (discontinued **)
Copyright © lookpolymers.com All Rights Reserved