Techmer ES Luriblend® POM HO TL20 BK Acetal
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, PTFE-Filled |
| Manufacturer | Techmer ES |
| Trade Name | Luriblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Luriblend® POM HO TL20 BK Acetal.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAdditive: PTFE Lubricant(20%)Features: Lubricated and HomopolymerAppearance: BlackInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ASTM D792 |
| Water Absorption | 0.15 % @Time 86400 sec |
0.15 % @Time 24.0 hour |
ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 79 | 79 | ASTM D785 |
| Tensile Strength, Yield | 48.3 MPa | 7000 psi | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Yield Strength | 75.8 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 2.76 GPa | 400 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Thickness 3.17 mm |
0.800 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 2.40 J/cm @Thickness 3.17 mm |
4.50 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 99.0 µm/m-°C | 55.0 µin/in-°F | ASTM D696 |
| Melting Point | 162 °C | 324 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C | 215 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 50 LS PA6, 50% glass fibre, light stability
- Objet FullCure® 870 Vero Black Resin for Rapid Prototyping
- Iran Petrochemical (PCC) 60505 High Density Polyethylene
- Haynes 188 alloy, plate at RT after 8000 hours at 760°C (1400°F)
- Solvay TECHNYL® A 402 Natural FA PA66, DRY
- SGL Carbon Group SIGRAFIL C® C25 S003 APS Staple Carbon Fiber, Aromatic Polymer Sizing
- Solvay IGEPAL® CO 997 Surfactant
- Tra-Con Tra-Bond 2122 Metal Repair Aluminum Epoxy Adhesive
- Entec Hylex® P1010L1 HB Polycarbonate
- Braskem LF 118/21 LLDPE Blown Film Extrusion Polyethylene Copolymer
Copyright © lookpolymers.com All Rights Reserved