Zotefoams Evazote® EV45CN Conductive Ethylene Vinyl Acetate Copolymer Foam

Category	Polymer , Thermoplastic , Ethylene Vinyl Acetate
Manufacturer	Zotefoams
Trade Name	Evazote®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Zotefoams Evazote® EV45CN Conductive Ethylene Vinyl Acetate Copolymer Foam.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Evazote® is a closed cell, cross-linked EVA copolymer foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outstanding physical attributes.Information provided by Zotefoams

Physical Properties	Metric	English	Comments
Density	0.0370 - 0.0490 g/cc	0.00134 - 0.00177 lb/in³	sheet density
	0.0450 g/cc	0.00163 lb/in³	Nominal skin/skin; BS ISO 7214 1998
Cell Length	0.200 - 0.600 mm	0.00787 - 0.0236 in
	0.400 mm	0.0157 in	Typical Diameter

Mechanical Properties	Metric	English	Comments
Hardness, Shore OO	52	52	10 mm cell/cell thickness; ISO 868 1985
Tensile Strength	0.575 MPa	83.4 psi	ISO 7214 1998
Elongation at Break	170 %	170 %
Compressive Yield Strength	0.0400 MPa @Strain 10.0 %	5.80 psi @Strain 10.0 %	BS ISO 7214 1998
	0.0610 MPa @Strain 25.0 %	8.85 psi @Strain 25.0 %	BS ISO 7214 1998
	0.0940 MPa @Strain 40.0 %	13.6 psi @Strain 40.0 %	BS ISO 7214 1998
	0.128 MPa @Strain 50.0 %	18.6 psi @Strain 50.0 %	BS ISO 7214 1998
Tear Strength	1.24 kN/m	7.08 pli	BS EN ISO 8067 1995
Compression Set	3.5 % @Time 79200 sec, Strain 25.0 %	3.5 % @Time 22.0 hour, Strain 25.0 %	24 hr recovery; BS ISO 7214 1998
	9.5 % @Time 79200 sec, Strain 25.0 %	9.5 % @Time 22.0 hour, Strain 25.0 %	0.5 hr recovery; BS ISO 7214 1998
	14.5 % @Time 79200 sec, Strain 50.0 %	14.5 % @Time 22.0 hour, Strain 50.0 %	24 hr recovery; BS ISO 7214 1998
	22 % @Time 79200 sec, Strain 50.0 %	22 % @Time 22.0 hour, Strain 50.0 %	0.5 hr recovery; BS ISO 7214 1998

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.0380 W/m-K	0.264 BTU-in/hr-ft²-°F	mean temp of 10°C; ISO 8302 1991
Maximum Service Temperature, Air	70.0 °C	158 °F
Minimum Service Temperature, Air	-70.0 °C	-94.0 °F
Flammability Test	0.70 @Thickness 13.0 mm	0.70 @Thickness 0.512 in	Horizontal Burn Rate, mm/sec; ISO 7214 1998
	1.3 @Thickness 5.00 mm	1.3 @Thickness 0.197 in	Horizontal Burn Rate, mm/sec; ISO 7214 1998

Electrical Properties	Metric	English	Comments
Volume Resistivity	1000 ohm-cm	1000 ohm-cm	ASTM D991-89

Descriptive Properties	Value	Comments
Flammability	Automotive: FMVSS.302 burn rate	Pass: 5mm and thicker