Lubrizol ESTALOC® 59200 Ester-Type, Reinforced Engineering Thermoplastic (European Grade)

Category	Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Glass Filled
Manufacturer	Lubrizol (former Noveon)
Trade Name	ESTALOC®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lubrizol ESTALOC® 59200 Ester-Type, Reinforced Engineering Thermoplastic (European Grade).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Estaloc® RETP (Reinforced Engineering Thermoplastic) is a tough, dimensionally stable, abrasion-resistant thermoplastic that withstands demanding environments. Developed as an extension to the Noveon Estane® TPU technology, Estaloc® RETP products complement Estane's durability and aesthetics with increased stiffness capability and dimensional stability over a broad temperature performance range not available from other engineering thermoplastics.Major Benefits of Estaloc® RETPs: Superior Dimensional Stability approaching that of metalsClass A surface aestheticsPaintability with no primer nor adhesion promoterExcellent abrasion and scuff/mar resistanceToughness over a broad temperature rangeExcellent adhesion to a variety of overmolding chemistriesInformation provided by Noveon, Inc.

Physical Properties	Metric	English	Comments
Specific Gravity	1.44 g/cc	1.44 g/cc	ISO 1183
Filler Content	30 %	30 %
Linear Mold Shrinkage	0.0015 cm/cm	0.0015 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	68	68	ISO 868
Tensile Strength, Ultimate	74.0 MPa	10700 psi	ISO 527-2/1A/5
Elongation at Break	20 %	20 %	ISO 527-2/1A/5
Tensile Modulus	2.883 GPa	418.2 ksi	ISO 527-2/1A/1
Flexural Strength	67.0 MPa	9720 psi	ISO 178
Flexural Modulus	2.36 GPa	342 ksi	ISO 178
Izod Impact, Notched (ISO)	25.0 kJ/m²	11.9 ft-lb/in²	Low Temp; ISO 180/1eA
	70.0 kJ/m²	33.3 ft-lb/in²	ISO 180/1eA
Izod Impact, Unnotched (ISO)	NB	NB	ISO 180/1eU
	95.0 kJ/m² @Temperature -30.0 °C	45.2 ft-lb/in² @Temperature -22.0 °F	ISO 180/1eU
Charpy Impact Unnotched	14.4 J/cm²	68.5 ft-lb/in²	ISO 179/1eU
	103 J/cm² @Temperature -30.0 °C	490 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
Charpy Impact, Notched	5.80 J/cm²	27.6 ft-lb/in²	ISO 179/1eA
	2.00 J/cm² @Temperature -30.0 °C	9.52 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
Taber Abrasion, mg/1000 Cycles	20	20	CS-17 wheel; ASTM D1044

Thermal Properties	Metric	English	Comments
CTE, linear	13.5 µm/m-°C @Temperature 20.0 °C	7.50 µin/in-°F @Temperature 68.0 °F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	154 °C	309 °F	method Bf; ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi)	126 °C	259 °F	method Af; ISO 75-2
Vicat Softening Point	107 °C	225 °F	temperature B; ISO 36
	176 °C	349 °F	temperature A; ISO 306