Techmer ES Luriblend® POM HO TL20 Acetal
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, PTFE-Filled |
| Manufacturer | Techmer ES |
| Trade Name | Luriblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Luriblend® POM HO TL20 Acetal.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAdditive: PTFE Lubricant(20%)Features: Lubricated and HomopolymerInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ASTM D792 |
| Water Absorption | 0.15 % @Time 86400 sec |
0.15 % @Time 24.0 hour |
ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 79 | 79 | ASTM D785 |
| Tensile Strength, Yield | 49.6 MPa | 7200 psi | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Yield Strength | 77.9 MPa | 11300 psi | ASTM D790 |
| Flexural Modulus | 2.76 GPa | 400 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm @Thickness 3.17 mm |
0.900 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 2.40 J/cm @Thickness 3.17 mm |
4.50 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 99.0 µm/m-°C | 55.0 µin/in-°F | ASTM D696 |
| Melting Point | 162 °C | 324 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C | 215 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- LyondellBasell Petrothene® LP540200 High Density Polyethylene, Film Extrusion Grade
- Huntsman Araldite ECN 1273 Epoxy Cresol Novolac
- ICO Polymers ICOFLOâ„¢ 510-5053 500 Micron LDPE Powder
- LG Chemical LUMID HI1102B(W) PA66, High Impact
- A. Schulman POLYBATCH™ Green 300 Concentrate Based In Polyethylene
- Covestro Bayblend® W85 HI PC ASA Blend
- Dow 722 Low Density Polyethylene (LDPE)
- ATI Allvac® 720 Nickel Superalloy, Heat Treatment: 1093°C (2000°F) + Age
- Technetics Group PLASTOLON™ Skived PTFE Tape (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved