SABIC Innovative Plastics LNP LUBRICOMP UFL36AS PPA (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP UFL36AS PPA (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* UFL36AS is a compound based on Polyphthalamide resin containing Glass Fiber, PTFE. Added features include Internally Lubricated, Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 190 MPa | 27600 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.1 % | 2.1 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 10.6 GPa | 1540 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 250 MPa | 36300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 9.90 GPa | 1440 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.48 | 0.48 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.52 | 0.52 | ASTM D3702 Modified |
| K (wear) Factor | 10.1 x 10-8 mm³/N-M | 5.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
12.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 58.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
32.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 4404 PPC+PC
- DuPont Performance Polymers Delrin® 911DP BK402 Acetal Homopolymer (Unverified Data**)
- Hexion Bakelite™ X22 Phenolic Formaldehyde Resin, UL Listed (discontinued **)
- LG Chemical SBR 1789 High Acrylonitrile Polymer
- Techmer ES Luriblend® PPA CF30 TL15 30% Carbon Filled
- Excalibar NewWate™ Barite BaSO4 Powder
- China Tungsten FeMo60-B Ferro Molybdenum
- Chosun Refractories HSC-85AL Dense and High-Strength Castable, Credens
- Barlog Plastics KEBAFLEX SG 55 A.01 TPE-S, Shore A55, natural
- Haynes 625 alloy, 40% cold reduction
Copyright © lookpolymers.com All Rights Reserved