- Techmer ES HiFill® PPS GF/M55 BK 55% Glass/Mineral Filled
Techmer ES HiFill® PPS GF/M55 BK 55% Glass/Mineral Filled
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® PPS GF/M55 BK 55% Glass/Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass/Mineral, 55% Filler by WeightAppearance: BlackInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.80 g/cc | 0.0650 lb/in³ | ASTM D792 |
| Water Absorption | 0.040 % @Time 86400 sec |
0.040 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 3.17 mm |
0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength, Yield | 162 MPa | 23500 psi | ASTM D638 |
| Elongation at Break | 1.5 % | 1.5 % | ASTM D638 |
| Flexural Yield Strength | 250 MPa | 36300 psi | ASTM D790 |
| Flexural Modulus | 16.2 GPa | 2350 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm @Thickness 3.17 mm |
1.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 19.8 µm/m-°C | 11.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 282 °C | 540 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 271 °C | 520 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 22.0 kV/mm | 560 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- MV Labs HO100 Ho(C2H3O2)3·xH2O Holmium acetate hydrate
- SABIC Innovative Plastics Lexan® 4501 PPC (Asia Pacific)
- Kennametal Stellite Stellite® F Cobalt Alloy
- Taiwan Sheen Soon Sheenthane® A7551E2 Thermoplastic Polyurethane Elastomer
- Stir SpA C 2004 91 D AT (PVC)
- A. Schulman POLYFORT™ FPP 3391 Chemically Coupled, Modified Polypropylene
- 3M 7142 Repositionable Paper Label Material
- Asahi Glass ASAHIKLIN AK-225DH Hydrochlorofluorocarbon Solvent
- Ineos Nova 207 Crystal Polystyrene High Heat, High Flow Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved