Techmer ES HiFill® POM CO GC20 20% Glass Bead Filled
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Glass Bead Filled |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® POM CO GC20 20% Glass Bead Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Bead, 20% Filler by WeightFeatures: CopolymerInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | ASTM D792 |
| Water Absorption | 0.50 % @Time 86400 sec |
0.50 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.014 cm/cm @Thickness 3.17 mm |
0.014 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 75 | 75 | ASTM D785 |
| Tensile Strength, Yield | 51.7 MPa | 7500 psi | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Yield Strength | 81.4 MPa | 11800 psi | ASTM D790 |
| Flexural Modulus | 3.38 GPa | 490 ksi | ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm @Thickness 3.17 mm |
0.700 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 63.0 µm/m-°C | 35.0 µin/in-°F | ASTM D696 |
| Melting Point | 166 °C | 330 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 310 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 117 °C | 242 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 17.7 kV/mm | 450 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- MV Labs AL500 AlF3 Aluminum fluoride, anhydrous
- S&E Specialty Polymers G-4275E
- Nilit FRIANYL A63 GV15 Nylon 6.6 for injection molding, 15% glass fiber reinforced
- Reade Advanced Materials Chromium Trioxide (CrO3)
- Lotte Chemical Titan TITANPRO® PM655 Polypropylene homopolymer
- Lubriplate Lithium Brick Grease Specialty Lubricant and Grease
- Spartech 2946-96A General Purpose PVC
- Spartech Royalite R66 PVC/Acrylic Fire Rated Sheet
- ExxonMobil LD331.99 EVA LD 331.99 Very Clear, High Impact Film Resin
- Owens Corning Glass Fiber Reinforced Polyester SMC (Compression), 50 wt.% glass
Copyright © lookpolymers.com All Rights Reserved