Techmer ES HiFill FR® PA6/6 GF25 FR-N IM3 BK 25% Glass Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled , Nylon 66, Impact Grade |
| Manufacturer | Techmer ES |
| Trade Name | HiFill FR® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill FR® PA6/6 GF25 FR-N IM3 BK 25% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 25% Filler by WeightAdditive: Impact ModifierFeatures: Flame Retardant, Halogen Free and Impact ModifiedAppearance: BlackInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D792 |
| Water Absorption | 0.95 % @Time 86400 sec |
0.95 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 3.17 mm |
0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 94 | 94 | ASTM D785 |
| Tensile Strength, Yield | 152 MPa | 22000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 200 MPa | 29000 psi | ASTM D790 |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
1.30 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| 1.07 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
2.00 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 9.61 J/cm @Thickness 3.17 mm |
18.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 36.0 µm/m-°C | 20.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| 5VB @Thickness 2.00 mm |
5VB @Thickness 0.0787 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | ASTM D257 |
| Dielectric Strength | 20.5 kV/mm | 520 kV/in | Method A (Short-Time); ASTM D149 |
| Comparative Tracking Index | >= 550 V | >= 550 V | UL 746 |
Users viewing this material also viewed the following:
- MV Labs EU800 Eu2O3 Europium(III) oxide
- MV Labs SR880 Sr(OH)2·8H2O Strontium hydroxide octahydrate
- Network Polymers Softflex® 0826
- MarkeTech Repton 201 Aluminum Oxide
- Gouda Vuurvast CURAS 90 PF REPAIR Moldable Refractory Material
- SABIC Innovative Plastics LNP VERTON RV008ES PA 66 (Asia Pacific)
- Wellman Wellamid® GF30-60 42LH-NBK1 30% Glass Fiber Reinforced Nylon 6
- CP-Polymer-Technik Wellamid® 6000 GX 350 HWCP Combination Nylon 6, Heat Stabilized, Conditioned
- E-Polymers TEKANATE™ G730 , 30% Glass Fiber Reinforced Poly Carbonate
Copyright © lookpolymers.com All Rights Reserved