Techmer ES Electrablend® PA6/6 CF20 L 20% Carbon Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Carbon Fiber Filled , Nylon 66, Conductive |
| Manufacturer | Techmer ES |
| Trade Name | Electrablend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Electrablend® PA6/6 CF20 L 20% Carbon Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber Reinforcement, 20% Filler by WeightAdditive: LubricantFeatures: Semi Conductive and LubricatedInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| Water Absorption | 0.85 % @Time 86400 sec |
0.85 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 3.17 mm |
0.0050 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Yield | 179 MPa | 26000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 276 MPa | 40000 psi | ASTM D790 |
| Flexural Modulus | 16.2 GPa | 2350 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm @Thickness 3.17 mm |
1.20 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.4 µm/m-°C | 38.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 259 °C | 498 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+7 ohm-cm | 1.00e+7 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+7 ohm | 1.00e+7 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Nilit FRIANYL C73 MG40 Nylon 6.6/6 for injection molding, 40% mineral filled
- EVALCA EVAL® K102 Ethylene Vinyl Alcohol Copolymer Resin (discontinued **)
- Arlon A3020-T002-12 Silicone Rubber/Fiberglass Laminate (discontinued **)
- Karina 600/167-IE MBPP Blue Color Concentrate
- Haynes 188 alloy, plate at RT after 0 hours at 870°C (1600°F)
- Techmer ES HiFill® PA6 GF33 HS L 33% Glass Filled
- Chase Plastics CP Pryme® N340MGL (COND, 50% RH) Nylon 6 (Utility Grade), 40% Mineral/Glass Fiber Reinforced, Internally Lubricated
- TIMET TIMETAL® 50A CP Titanium (ASTM Grade 2)
- ExxonMobil Mobil Rarus 1024 SHC 1000 Series
- LATI Lastil G/30 SAN, 30% Glass Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved