Network Polymers MS 200 Styrene Methyl Methacrylate Copolymer
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Polystyrene (PS) , Styrene/Methyl Methacrylate Copolymer (SMMA) |
| Manufacturer | Network Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Network Polymers MS 200 Styrene Methyl Methacrylate Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Styrene Methyl Methacrylate CopolymerInformation provided by Network Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Water Absorption | 0.11 % | 0.11 % | 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 2.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 75 | 75 | ASTM D785 |
| Tensile Strength, Yield | 57.23 MPa | 8301 psi | 2 in per min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 3.13 GPa | 454 ksi | ASTM D638 |
| Izod Impact, Notched | 0.160 J/cm | 0.300 ft-lb/in | 0.125 inch bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C | 169 °F | ASTM D648 |
| Vicat Softening Point | 97.7 °C | 208 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | ASTM D1003 |
Users viewing this material also viewed the following:
- Petroquimica Triunfo Trithene® TS 7006 LDPE - Coextruded Film
- Techmer ES HiFill® PA6 GF33 IM L UV 33% Glass Filled
- Washington Penn Medium Impact Copolymer 10% Calcium Carbonate Filled
- DSM Akulon® K125 PA6
- EMS-Griltech Griltex® 6E Copolyester Hotmelt Adhesive (Technical Applications)
- Braskem F020HC High Crystallinity Polypropylene Homopolymer
- BASF N4-Amine S N,N'-Bis-(3-Aminopropyl)ethylene-diamine
- 3M Scotch-Weld™ 847 Nitrile High Performance Rubber & Gasket Adhesive
- Asahi Glass Fluon® PA1025Z 25% Glass Fiber, PTFE Filled Compound
Copyright © lookpolymers.com All Rights Reserved